- We present comparative characteristics of microwave variable capacitors (varactors) fabricated on Na0.5K0.5NbO3 (NKN), AgTa0.5Nb0.5O3 (ATN) and Ba0.5Sr0.5TiO3 (BST) ferroclectric films sintered by pulsed laser deposition technique. Two port 2 mu m finger gap coplanar waveguide interdigital capacitive (CPWIDC) structures were defined on ferroelectric films surface by a standard lift off technique. Results of the microwave on-wafer tests performed in frequency range 1 to 40 GHz have been examined with a de-embedding technique to extract device characteristics from the measured S-parameters. The frequency dispersion of capacitance was 37%, 4.3%, and 17%; the voltage tunability (200 kV/cm) 22%, 4.7%, and 22% at 20 GHz; loss tangent similar to 0.23, 0.068, and 0.137 at 20 GHz for NKN/Nd:YAlO3, ATN/Al2O3, and BST/Al2O3 films capacitors.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Elektroteknik och elektronik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Electrical Engineering, Electronic Engineering, Information Engineering (hsv//eng)
Nyckelord
- ferroelectric ceramics
- pulsed laser deposition
- epitaxial films
- pottasium sodium niobate
- silver tantalate niobate
- barium strontium titanate
- coplanar waveguides
- voltage tunable microwave devices
- scattering parameters measurement
- Electrical engineering, electronics and photonics
- Elektroteknik, elektronik och fotonik
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas