(författare)
Molecular weight changes and polymeric matrix changes correlated with the formation of degradation products in biodegraded polyethylene
- Artikel/kapitelEngelska1999
Förlag, utgivningsår, omfång ...
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:kth-72641
-
https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-72641URI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
NR 20140805
-
The molecular weight changes in abiotically and biotically degraded LDPE and LDPE modified with starch and/or prooxidant were compared with the formation of degradation products, The samples were thermooxidized for 6 days at 100 degrees C to initiate degradation and then either inoculated with Arthobacter paraffineus or kept sterile. After 3.5 years homologous series of mono- and dicarboxylic acids and ketoacids were identified by GC-MS in abiotic samples, while complete disappearance of these acids was observed in biotic environments. The molecular weights of the biotically aged samples were slightly higher than the molecular weights of the corresponding abiotically aged samples, which is exemplified by the increase in (M) over bar(n) from 5200 g/mol for a sterile sample with the highest amount of prooxidant to 6000 g/mol for the corresponding biodegraded sample. The higher molecular weight in the biotic environment is explained by the assimilation of carboxylic acids and low molecular weight polyethylene chains by microorganisms. Assimilation of the low molecular weight products is further confirmed by the absence of carboxylic acids in the biotic samples. Fewer carbonyls and more double bonds were seen by FTIR in the biodegraded samples, which is in agreement with the biodegradation mechanism of polyethylene.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Erlandsson, BengtKTH,Polymerteknologi
(författare)
-
Hakkarainen, MinnaKTH,Polymerteknologi(Swepub:kth)u14e229n
(författare)
-
Karlsson, SigbrittKTH,Polymerteknologi
(författare)
-
KTHPolymerteknologi
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Journal of environmental polymer degradation64, s. 91-991064-75461572-8900
Internetlänk
Hitta via bibliotek
Till lärosätets databas