Nano ZrO2/CoSb3 composites with improved thermoelectric figure of merit

• Nano ZrO2/CoSb3 composites with different ZrO 2 contents were prepared using hot pressing. The phase purity, the microstructure and the temperature-dependent transport parameters of the composites were investigated. The dimensionless figure of merit (ZT) of 0.18 of the non-dispersed CoSb3 preponderates the maximal value (0.17) of pure CoSb3 reported in the literature, which is attributed to the prepared sample having higher electrical conductivity due to the existence of a small amount of metallic Sb and lower thermal conductivity due to the fine-grained structure. Compared to non-dispersed CoSb3, a further improvement of 11% on ZT (0.20) was achieved in the composite with 0.05ZrO 2 inclusions, which resulted from the enhanced ratio of electrical conductivity to thermal conductivity and the Seebeck coefficient. The nanodispersion method provides an effective approach to improving a material's thermoelectric properties and performance.

Ämnesord

NATURVETENSKAP  -- Kemi -- Materialkemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Materials Chemistry (hsv//eng)

Nyckelord

Cobalt compounds

Electric conductivity

Hot pressing

Seebeck coefficient

Thermal conductivity

Zirconia

Materials chemistry

Materialkemi

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)