Heat treatment of black dross for the production of a value added material - a preliminary study
-
- Beheshti, Reza (författare)
- KTH,Materialens processvetenskap
-
Akhtar, Shahid (författare)
-
- Aune, Ragnhild E. (författare)
- KTH,Materialens processvetenskap
-
(creator_code:org_t)
- 2012-05-15
- 2012
- Engelska.
-
Ingår i: EPD Congress 2012. - Hoboken, NJ, USA : John Wiley & Sons. - 9781118291405 ; , s. 353-360
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The potential use of Black Dross (BD) as a raw material for the production of refractories, fluxing agents and glasses is the main motivation of the present study. Heat treatment experiments were carried out in Ar, and under reduced pressure (20 Pa), to evaluate the salt removal efficiency. The chemical composition of the BD after heat treatment was investigated by SEM-EDS and XRD analyses. Based on the present results, it is established that the salt starts to evaporate at ≈1273 K in Ar, and under reduced pressure. The salt removal efficiency in a 20 g sample was found to increase in both cases as a function of time and temperature. Moreover, in Ar the chlorine concentration was lowered to 0.3 wt% after heat treatment at 1523 K for 10 hours. Under reduced pressure, however, 0.2 wt% residual chlorine was obtained after 8 hours at 1473 K.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
Nyckelord
- Aluminum
- Black dross
- Heat treatment
- Waste processing