Physico-chemical properties of Chitosan films
-
- Balau, Luminita (författare)
- Department of Physical - Chemistry, Technical University, Gh. Asachi, Iasi, Romania
-
- Lisa, Gabriela (författare)
- Department of Physical - Chemistry, Technical University, Gh. Asachi, Iasi, Romania
-
- Popa, M. I. (författare)
- Department of Physical - Chemistry, Technical University, Gh. Asachi, Iasi, Romania
-
visa fler...
-
- Tura, V. (författare)
- Faculty of Physics, University, Al. I. Cuza, Iasi, Romania
-
- Melnig, V. (författare)
- Faculty of Physics, University, Al. I. Cuza, Iasi, Romania
-
visa färre...
-
Department of Physical - Chemistry, Technical University, Gh Asachi, Iasi, Romania Faculty of Physics, University, Al. I. Cuza, Iasi, Romania (creator_code:org_t)
- 2004
- 2004
- Engelska.
-
Ingår i: Central European Journal of Chemistry. - 1895-1066 .- 1644-3624. ; 2:4, s. 638-647
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.2...
-
visa färre...
Abstract
Ämnesord
Stäng
- Chitosan films obtained by dry phase inversion were prepared from an aqueous solution of chitosan in acetic acid. The films, of thickness less than 20 μm, were transparent, very flexible and had smooth surfaces. Increasing the film thickness induced an increase of the internal tensions and the consequent formation of a rough surface. Structural investigations by X-ray diffraction and Fourier transform IR analysis, showed that the chitosan films, as prepared, are amorphous. Further annealing to evaporate acetic acid and water traces, changed the amorphous phase into a more ordered phase, characterized by diffraction peaks at 2θ values of 9, 17, 20 and 23 degrees. Thermal investigations by TG, DTG, and DTA revealed that the decomposition of the chitosan films as prepared proceeds in two stages, starting from 180°C and 540°C.