Epitaxial growth of gamma-Al2O3 on Ti2AlC(0001) by reactive high-power impulse magnetron sputtering
-
- Eklund, Per (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska högskolan
-
- Frodelius, Jenny (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska högskolan
-
- Hultman, Lars (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska högskolan
-
visa fler...
-
- Lu, Jun (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska högskolan
-
- Magnfält, Daniel (författare)
- Linköpings universitet,Plasma och ytbeläggningsfysik,Tekniska högskolan
-
visa färre...
-
(creator_code:org_t)
- American Institute of Physics (AIP), 2014
- 2014
- Engelska.
-
Ingår i: AIP Advances. - : American Institute of Physics (AIP). - 2158-3226. ; 4:1, s. 017138-
- Relaterad länk:
-
https://liu.diva-por... (primary) (Raw object)
-
visa fler...
-
https://aip.scitatio...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Al2O3 was deposited by reactive high-power impulse magnetron sputtering at 600 degrees C onto pre-deposited Ti2AlC(0001) thin films on alpha-Al2O3(0001) substrates. The Al2O3 was deposited to a thickness of 65 nm and formed an adherent layer of epitaxial gamma-Al2O3(111) as shown by transmission electron microscopy. The demonstration of epitaxial growth of gamma-Al2O3 on Ti2AlC (0001) open prospects for growth of crystalline alumina as protective coatings on Ti2AlC and related nanolaminated materials. The crystallographic orientation relationships are gamma-Al2O3(111)//Ti2AlC(0001) (out-of-plane) and gamma-Al2O3(2 (2) over bar0)//Ti2AlC(11 (2) over bar0) (in-plane) as determined by electron diffraction. Annealing in vacuum at 900 degrees C resulted in partial decomposition of the Ti2AlC by depletion of Al and diffusion into and through the gamma-Al2O3 layer.