Nanostructuring and coherency strain in multicomponent hard coatings
-
- Forsén, Rikard (författare)
- Linköpings universitet,Tekniska högskolan,Teoretisk Fysik
-
- Schramm, I. C. (författare)
- Functional Materials, Department Materials Science, Saarland University, Saarbrücken, Germany
-
- Alling, Björn (författare)
- Linköpings universitet,Teoretisk Fysik,Tekniska högskolan
-
visa fler...
-
- Persson, Per O Å (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska högskolan
-
- Mücklich, F. (författare)
- Institute of Ion Beam Physics and Materials Research, Forschungszentrum Dresden-Rossendorf
-
- Odén, Magnus (författare)
- Linköpings universitet,Nanostrukturerade material,Tekniska högskolan
-
- Ghafoor, Naureen (författare)
- Linköpings universitet,Nanostrukturerade material,Tekniska högskolan
-
visa färre...
-
(creator_code:org_t)
- American Institute of Physics (AIP), 2014
- 2014
- Engelska.
-
Ingår i: APL Materials. - : American Institute of Physics (AIP). - 2166-532X. ; 2:11, s. 116104-
- Relaterad länk:
-
http://scitation.aip...
-
visa fler...
-
https://liu.diva-por... (primary) (Raw object)
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Lattice resolved and quantitative compositional characterizations of the microstructure in TiCrAlN wear resistant coatings emerging at elevated temperatures are performed to address the spinodal decomposition into nanometer-sized coherent cubic TiCr- and Al-rich domains. The domains coarsen during annealing and at 1100 ºC, the Al-rich domains include a metastable cubic Al(Cr)N phase containing 9 at.% Cr and a stable hexagonal AlN phase containing less than 1 at.% Cr. The cubic and the hexagonal phases form strained semi-coherent interfaces with each other.
Ämnesord
- NATURVETENSKAP -- Fysik (hsv//swe)
- NATURAL SCIENCES -- Physical Sciences (hsv//eng)
Nyckelord
- Age hardening; Spinodal decomposition; Cathodic arc evaporation; Aberration corrected TEM