Sökning: onr:"swepub:oai:DiVA.org:liu-115712" >
Application of weak...
Application of weak ferromagnetic BiFeO3 films as the photoelectrode material under visible-light irradiation
-
- Chen, X. Y. (författare)
- Nanjing University, Peoples R China
-
- Yu, T. (författare)
- Nanjing University, Peoples R China
-
- Gao, Feng (författare)
- Linköpings universitet,Biomolekylär och Organisk Elektronik,Tekniska högskolan
-
visa fler...
-
- Zhang, H. T. (författare)
- Nanjing University, Peoples R China
-
- Liu, L. F. (författare)
- Nanjing University, Peoples R China
-
- Wang, Y. M. (författare)
- Nanjing University, Peoples R China
-
- Li, Z. S. (författare)
- Nanjing University, Peoples R China
-
- Zou, Z. G. (författare)
- Nanjing University, Peoples R China
-
- Liu, J.-M. (författare)
- Nanjing University, Peoples R China
-
visa färre...
-
(creator_code:org_t)
- American Institute of Physics (AIP), 2007
- 2007
- Engelska.
-
Ingår i: Applied Physics Letters. - : American Institute of Physics (AIP). - 0003-6951 .- 1077-3118. ; 91:2, s. 022114-
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- BiFeO3 films prepared by pulsed laser deposition on Pt/TiO2/SiO2/Si substrates were studied as photoelectrode for water splitting. Under visible-light irradiation, the photocurrent intensity of the polycrystalline BiFeO3 film was found to double that of the amorphous one in a three-electrode cell. The incident photon to current conversion efficiency for the polycrystalline BiFeO3 electrode was approximately 16% at 350 nm and 7% at 530 nm at 1.5 V (versus saturated calomel electrode). The ferromagnetism of the amorphous BiFeO3 film was an order of magnitude weaker than that of the polycrystalline one, supporting the "size effect" explanation for magnetic origin. (C) 2007 American Institute of Physics.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas