Ti deficiency effect on the dielectric response of CaCu3Ti4O12 ceramics

Single phase ceramics CaCu3Ti4.0O12 and CaCu3Ti3.9O12 have been prepared using the traditional solid-state reaction method. Compared with the stoichiometric ceramics CaCu3Ti4.0O12, Ti-deficient ceramics CaCu3Ti3.9O12 have the larger lattice parameter, the higher force constant, and smaller dielectric constant and the lower dissipation factor, although their fundamental characters of dielectric response are similar. Their characteristic relaxation frequencies are not well fitted with the Arrhenius Law but a tentatively supposed relation. With the Cole-Cole Law, the fitted broadened factors of dissipation peaks are 0.5433 and 0.8651 for CaCu3Ti3.9O12 and CaCu3Ti4.0O12, respectively. All facts mentioned above imply that mutually correlated motion of Ti ions or defects may be expected to be responsible for the giant dielectric constant and high dissipation factor of CaCu3T4.0O12. (c) 2006 Elsevier Ltd. All rights reserved.

Liu, Y. F.Nanjing University, Peoples R China (författare)
Gao, FengLinköpings universitet,Biomolekylär och Organisk Elektronik,Tekniska högskolan(Swepub:liu)fenga88 (författare)
Du, Z. L.Nanjing University, Peoples R China (författare)
Liu, J. M.Nanjing University, Peoples R China (författare)
Ying, X. N.Nanjing University, Peoples R China (författare)
Lu, X. M.Nanjing University, Peoples R China (författare)
Zhu, J. S.Nanjing University, Peoples R China (författare)
Nanjing University, Peoples R ChinaBiomolekylär och Organisk Elektronik (creator_code:org_t)

Av författaren/redakt...: Chen, K.; Liu, Y. F.; Gao, Feng; Du, Z. L.; Liu, J. M.; Ying, X. N.; visa fler...; Lu, X. M.; Zhu, J. S.; visa färre...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.