Sökning: onr:"swepub:oai:DiVA.org:liu-165095" >
The effects of micr...
The effects of microstructure, Nb content and secondary Ruddlesden-Popper phase on thermoelectric properties in perovskite CaMn1-xNbxO3 (x=0-0.10) thin films
-
- Ekström, Erik (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Linköpings universitet, Tunnfilmsfysik
-
- Le Febvrier, Arnaud (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Linköpings universitet, Tunnfilmsfysik
-
- Bourgeois, F. (författare)
- Univ Technol Blois, France
-
visa fler...
-
- Lundqvist, Björn (författare)
- Linköpings universitet,Halvledarmaterial,Tekniska fakulteten,Linköpings universitet, Halvledarmaterial
-
- Palisaitis, Justinas (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Linköpings universitet, Tunnfilmsfysik
-
- Persson, Per O A (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Linköpings universitet, Tunnfilmsfysik
-
- Caballero-Calero, O. (författare)
- CEI UAM, Spain
-
- Martin-Gonzalez, M. S. (författare)
- CEI UAM, Spain,Linköpings universitet, Teoretisk Fysik
-
- Klarbring, Johan (författare)
- Linköpings universitet,Teoretisk Fysik,Tekniska fakulteten,Linköpings universitet, Teoretisk Fysik
-
- Simak, Sergey (författare)
- Linköpings universitet,Teoretisk Fysik,Tekniska fakulteten
-
- Eriksson, Fredrik (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Linköpings universitet, Tunnfilmsfysik
-
- Paul, Biplab (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Linköpings universitet, Tunnfilmsfysik
-
- Eklund, Per (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Linköpings universitet, Tunnfilmsfysik
-
visa färre...
-
(creator_code:org_t)
- 2020
- 2020
- Engelska.
-
Ingår i: RSC Advances. - : Royal Society of Chemistry. - 2046-2069. ; 10:13, s. 7918-7926
- Relaterad länk:
-
https://liu.diva-por... (primary) (Raw object)
-
visa fler...
-
https://pubs.rsc.org...
-
https://doi.org/10.1...
-
https://uu.diva-port... (primary) (Raw object)
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- CaMn1-xNbxO3 (x = 0, 0.5, 0.6, 0.7 and 0.10) thin films have been grown by a two-step sputtering/annealing method. First, rock-salt-structured (Ca,Mn1-x,Nb-x)O thin films were deposited on 11 & x304;00 sapphire using reactive RF magnetron co-sputtering from elemental targets of Ca, Mn and Nb. The CaMn1-xNbxO3 films were then obtained by thermally induced phase transformation from rock-salt-structured (Ca,Mn1-xNbx)O to orthorhombic during post-deposition annealing at 700 degrees C for 3 h in oxygen flow. The X-ray diffraction patterns of pure CaMnO3 showed mixed orientation, while Nb-containing films were epitaxially grown in [101] out of-plane-direction. Scanning transmission electron microscopy showed a Ruddlesden-Popper (R-P) secondary phase in the films, which results in reduction of the electrical and thermal conductivity of CaMn1-xNbxO3. The electrical resistivity and Seebeck coefficient of the pure CaMnO3 film were measured to 2.7 omega cm and -270 mu V K-1 at room temperature, respectively. The electrical resistivity and Seebeck coefficient were reduced by alloying with Nb and was measured to 0.09 omega cm and -145 mu V K-1 for x = 0.05. Yielding a power factor of 21.5 mu W K-2 m(-1) near room temperature, nearly eight times higher than for pure CaMnO3 (2.8 mu W K-2 m(-1)). The power factors for alloyed samples are low compared to other studies on phase-pure material. This is due to high electrical resistivity originating from the secondary R-P phase. The thermal conductivity of the CaMn1-xNbxO3 films is low for all samples and is the lowest for x = 0.07 and 0.10, determined to 1.6 W m(-1) K-1. The low thermal conductivity is attributed to grain boundary scattering and the secondary R-P phase.
Ämnesord
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Ekström, Erik
-
Le Febvrier, Arn ...
-
Bourgeois, F.
-
Lundqvist, Björn
-
Palisaitis, Just ...
-
Persson, Per O A
-
visa fler...
-
Caballero-Calero ...
-
Martin-Gonzalez, ...
-
Klarbring, Johan
-
Simak, Sergey
-
Eriksson, Fredri ...
-
Paul, Biplab
-
Eklund, Per
-
visa färre...
- Om ämnet
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Kemi
-
och Materialkemi
- Artiklar i publikationen
-
RSC Advances
- Av lärosätet
-
Linköpings universitet
-
Uppsala universitet