Fatigue crack growth for through and part-through cracks in additively manufactured Ti6Al4V
-
- Kahlin, Magnus, 1982- (författare)
- Linköpings universitet,Konstruktionsmaterial,Tekniska fakulteten,Saab AB, Aeronautics, Linköping, Sweden
-
- Ansell, Hans (författare)
- Linköpings universitet,Mekanik och hållfasthetslära,Tekniska fakulteten,Saab AB, Aeronautics, Linköping, Sweden
-
- Moverare, Johan, 1973- (författare)
- Linköpings universitet,Konstruktionsmaterial,Tekniska fakulteten
-
(creator_code:org_t)
- Elsevier, 2022
- 2022
- Engelska.
-
Ingår i: International Journal of Fatigue. - : Elsevier. - 0142-1123 .- 1879-3452. ; 155
- Relaterad länk:
-
https://doi.org/10.1...
-
visa fler...
-
https://liu.diva-por... (primary) (Raw object)
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Critical aerospace parts require damage tolerance analysis to determine the inspection intervals in-service. Such analyses, based on linear fracture mechanics, require that the fatigue crack growth (FCG) rate relation to the stress intensity factor range is applicable independent of geometry and stress. FCG rates for laser powder bed fusion Ti6Al4V material for conventional compact tension (CT) specimens have therefore been compared to FCG rates for specimens with a crack configuration more technically relevant from an industrial and engineering perspective. The FCG rates corresponded very well and data obtained with CT-specimens can therefore be considered relevant for general damage tolerance predictions.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- Additive manufacturing
- Ti6Al4V
- Fatigue crack growth
- Damage tolerance
- Aerospace