Mechanically Flexible Thermoelectric Hybrid Thin Films by Introduction of PEDOT:PSS in Nanoporous Ca3Co4O9
-
- Xin, Binbin (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Linköpings universitet, Tunnfilmsfysik
-
- Wang, Lei (författare)
- Linköpings universitet,Elektroniska och fotoniska material,Tekniska fakulteten,Linköpings universitet, Elektroniska och fotoniska material
-
- Le Febvrier, Arnaud (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Linköpings universitet, Tunnfilmsfysik
-
visa fler...
-
- Elsukova, Anna (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Linköpings universitet, Tunnfilmsfysik
-
- Paul, Biplab (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Linköpings universitet, Tunnfilmsfysik
-
- Solin, Niclas (författare)
- Linköpings universitet,Elektroniska och fotoniska material,Tekniska fakulteten,Linköpings universitet, Elektroniska och fotoniska material
-
- Eklund, Per (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Linköpings universitet, Tunnfilmsfysik
-
visa färre...
-
(creator_code:org_t)
- 2022-06-28
- 2022
- Engelska.
-
Ingår i: ACS Omega. - : American Chemical Society (ACS). - 2470-1343. ; 7:27, s. 23988-23994
- Relaterad länk:
-
https://liu.diva-por... (primary) (Raw object)
-
visa fler...
-
https://doi.org/10.1...
-
https://uu.diva-port... (primary) (Raw object)
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- Nanoporous Ca3Co4O9 exhibits high thermoelectric properties and low thermal conductivity and can be made mechanically flexible by nanostructural design. To improve the mechanical flexibility with retained thermoelectric properties near room temperature, however, it is desirable to incorporate an organic filler in this nanoporous inorganic matrix material. Here, double-layer nanoporous Ca3Co4O9/PEDOT:PSS thin films were synthesized by spin-coating PEDOT:PSS into the nanopores. The obtained hybrid films exhibit high Seebeck coefficient (~+130 mu V/K) and thermoelectric power factor (0.75 mu W cm(-1) K-2) at room temperature with no deterioration in electrical properties after cyclic bending tests (98% preservation of electrical conductivity after 1000 cycles bending to a bending radius of 3 mm). Compared with the nanoporous Ca3Co4O9 thin film, the mechanical flexibility of the hybrid film can be effectively improved after hybrid with PEDOT:PSS with only a slight decrease of the thermoelectric properties.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Textil-, gummi- och polymermaterial (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Textile, Rubber and Polymeric Materials (hsv//eng)
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas