Oxidation kinetics of overstoichiometric TiB2 thin films grown by DC magnetron sputtering
-
- Dorri, Samira, 1988- (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten
-
- Palisaitis, Justinas, 1983- (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten
-
- Greczynski, Grzegorz, 1973- (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten
-
visa fler...
-
- Petrov, Ivan, 1949- (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,University of Illinois at Urbana-Champaign, USA; National Taiwan University of Science and Technology, Taiwan
-
- Birch, Jens, 1960- (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten
-
- Hultman, Lars, Professor, 1960- (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten
-
- Bakhit, Babak, 1983- (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten
-
visa färre...
-
(creator_code:org_t)
- Pergamon-Elsevier Science Ltd, 2022
- 2022
- Engelska.
-
Ingår i: Corrosion Science. - : Pergamon-Elsevier Science Ltd. - 0010-938X .- 1879-0496. ; 206
- Relaterad länk:
-
https://doi.org/10.1...
-
visa fler...
-
https://liu.diva-por... (primary) (Raw object)
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- We systematically study the oxidation properties of sputter-deposited TiB2.5 coatings up to 700 °C. Oxide-scale thickness dox increases linearly with time ta for 300, 400, 500, and 700 °C, while an oxidation-protective behavior occurs with dox=250∙ta0.2 at 600 °C. Oxide-layer’s structure changes from amorphous to rutile/anatase-TiO2 at temperatures ≥ 500 °C. Abnormally low oxidation rate at 600 °C is attributed to a highly dense columnar TiO2-sublayer growing near oxide/film interface with a top-amorphous thin layer, suppressing oxygen diffusion. A model is proposed to explain the oxide-scale evolution at 600 °C. Decreasing heating rate to 1.0 °C/min plays a noticeable role in the TiB2.5 oxidation.
Ämnesord
- NATURVETENSKAP -- Fysik (hsv//swe)
- NATURAL SCIENCES -- Physical Sciences (hsv//eng)
Nyckelord
- Sputtering
- Thin films
- Titanium diboride (TiB)
- Microstructure
- Oxidation
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Dorri, Samira, 1 ...
-
Palisaitis, Just ...
-
Greczynski, Grze ...
-
Petrov, Ivan, 19 ...
-
Birch, Jens, 196 ...
-
Hultman, Lars, P ...
-
visa fler...
-
Bakhit, Babak, 1 ...
-
visa färre...
- Om ämnet
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Fysik
- Artiklar i publikationen
-
Corrosion Scienc ...
- Av lärosätet
-
Linköpings universitet