A Highly Reversible Aqueous Ammonium-Ion Battery based on alpha-MoO3/Ti3C2Tz Anodes and (NH4)(x)MnO2/CNTs Cathodes

  • Artikel/kapitelEngelska2023

Förlag, utgivningsår, omfång ...

  • 2023-01-18
  • WILEY-V C H VERLAG GMBH,2023
  • electronicrdacarrier

Nummerbeteckningar

  • LIBRIS-ID:oai:DiVA.org:liu-191985
  • https://urn.kb.se/resolve?urn=urn:nbn:se:liu:diva-191985URI
  • https://doi.org/10.1002/batt.202200432DOI

Kompletterande språkuppgifter

  • Språk:engelska
  • Sammanfattning på:engelska

Ingår i deldatabas

Klassifikation

  • Ämneskategori:ref swepub-contenttype
  • Ämneskategori:art swepub-publicationtype

Anmärkningar

  • Funding Agencies|Knut and Alice Wallenberg (KAW) Foundation for a Fellowship/Scholar Grant [KAW 2020.0033]; China Postdoctoral Science Foundation [2020TQ0063, 2021M700759]; Jiangsu Planned Projects for Postdoctoral Research Funds; Fundamental Research Funds for the Central Universities; Zhishan Youth Scholar Program of Southeast University
  • Aqueous ammonium-ion batteries (AAIBs) are appealing due to their relatively low cost and good rate performance. In general, AAIBs are environmentally friendlier than their non-aqueous counterparts. However, it is still a challenge to achieve highly reversible AAIBs with decent voltages and energy/power densities. Herein, we report on a full-cell configuration using alpha-MoO3/Ti3C2Tz films as anodes, and (NH4)(x)MnO2/CNTs films as cathodes in a 1 M ammonium acetate (NH4Ac) electrolyte. At 2 V, the operating cell voltage, OCV, is one of the highest reported for AAIBs. A maximum energy density of similar to 32 Wh kg(-1) (similar to 54 Wh L-1) at 0.2 A g(-1) and a maximum power density of similar to 10 kW kg(-1) (similar to 17 kW L-1) at 10 A g(-1) are attained. When the full cells are cycled 2,000 times at 1 A g(-1) they retain similar to 73 % of their initial capacity. When cycling at 10 A g(-1), similar to 96 % of capacity is retained after 43,500 cycles. After 10 h, self-discharge reduces the OCV to similar to 72 % of its original value. This work provides a roadmap for developing high performance AAIBs with high voltages and high energy/power densities. Before this is possible it is imperative that the self-discharge rate be substantially reduced.

Ämnesord och genrebeteckningar

Biuppslag (personer, institutioner, konferenser, titlar ...)

  • Zheng, WeiSoutheast Univ, Peoples R China (författare)
  • Halim, JosephLinköpings universitet,Materialdesign,Tekniska fakulteten(Swepub:liu)josha78 (författare)
  • Rosén, JohannaLinköpings universitet,Materialdesign,Tekniska fakulteten(Swepub:liu)johro07 (författare)
  • Sun, ZhengMingSoutheast Univ, Peoples R China (författare)
  • Barsoum, MichelLinköpings universitet,Materialdesign,Tekniska fakulteten,Drexel Univ, PA 19104 USA(Swepub:liu)micba79 (författare)
  • Linköpings universitetMaterialdesign (creator_code:org_t)

Sammanhörande titlar

  • Ingår i:Batteries & Supercaps: WILEY-V C H VERLAG GMBH62566-6223

Internetlänk

Hitta via bibliotek

Till lärosätets databas

Hitta mer i SwePub

Av författaren/redakt...
Yang, Li
Zheng, Wei
Halim, Joseph
Rosén, Johanna
Sun, ZhengMing
Barsoum, Michel
Om ämnet
TEKNIK OCH TEKNOLOGIER
TEKNIK OCH TEKNO ...
och Naturresurstekni ...
och Energisystem
Artiklar i publikationen
Batteries & Supe ...
Av lärosätet
Linköpings universitet

Sök utanför SwePub

Wikipedia om författaren:
Li_Yang
Yang, Li
en

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy