The inhibiting effect of Re-rich layer on the interdiffusion between NiAl and Ni3Al-based superalloy and its degradation
-
- Li, Jingchen (författare)
- Beihang Univ BUAA, Peoples R China
-
- Wu, Yuting (författare)
- Beihang Hangzhou Innovat Inst Yuhang, Peoples R China
-
- Liu, Liang (författare)
- Beihang Univ BUAA, Peoples R China
-
visa fler...
-
- Peng, Ru (författare)
- Linköpings universitet,Konstruktionsmaterial,Tekniska fakulteten
-
- Xu, Jinghao (författare)
- Linköpings universitet,Konstruktionsmaterial,Tekniska fakulteten
-
- He, Jian (författare)
- Beihang Univ BUAA, Peoples R China; Beihang Univ BUAA, Peoples R China; Beihang Hangzhou Innovat Inst Yuhang, Peoples R China
-
- Guo, Hongbo (författare)
- Beihang Univ BUAA, Peoples R China; Beihang Univ BUAA, Peoples R China; Beihang Univ BUAA, Peoples R China
-
visa färre...
-
(creator_code:org_t)
- ELSEVIER SCIENCE SA, 2023
- 2023
- Engelska.
-
Ingår i: Journal of Alloys and Compounds. - : ELSEVIER SCIENCE SA. - 0925-8388 .- 1873-4669. ; 957
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- A NiAl alloy/ Ni3Al-based superalloy diffusion couple with an electroplated NiRe layer was prepared. High-temperature interdiffusion performance of the diffusion couple was analyzed at 1100 degrees C under argon at-mosphere and compared with that of the blank group without NiRe layer. A Re-based diffusion barrier formed during the diffusion. The microstructural instability of the superalloy was found to be alleviated by the Re-based diffusion barrier, and the detailed microstructure of the diffusion barrier was identified to be Re-rich a phases and Mo-rich << phase detected by TEM. The chemical diffusion coefficient of Al was reduced by about two orders of magnitude with the modification of the Re-based diffusion barrier. A microstructural degradation of the Re-based barrier layer was observed after high-temperature diffusion of 300 h, which can be attributed to the internal diffusion of Mo.(c) 2023 Elsevier B.V. All rights reserved.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- Superalloy; Diffusion barrier; Diffusion couple; Interdiffusion; Interfaces