Annealing studies of nanocomposite Ti-Si-C thin films with respect to phase stability and tribological performance
-
Rester, M. (författare)
-
- Neidhardt, Jörg, 1976- (författare)
- Linköpings universitet,Tekniska högskolan,Tunnfilmsfysik
-
- Eklund, Per, 1977- (författare)
- Linköpings universitet,Tekniska högskolan,Tunnfilmsfysik
-
visa fler...
-
- Emmerlich, Jens, 1974- (författare)
- Linköpings universitet,Tekniska högskolan,Tunnfilmsfysik
-
Ljungcrantz, H. (författare)
-
- Hultman, Lars, 1960- (författare)
- Linköpings universitet,Tekniska högskolan,Tunnfilmsfysik
-
Mitterer, C. (författare)
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2006
- 2006
- Engelska.
-
Ingår i: Materials Science & Engineering. - : Elsevier BV. - 0921-5093 .- 1873-4936. ; 429:1-2, s. 90-95
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Nanocomposite Ti-Si-C thin films were deposited by dc magnetron sputtering from a Ti3SiC2 target onto Si(1 0 0) and high-speed steel substrates at 300 °C. The as-deposited films consisted of nanocrystalline (nc-) TiCx and amorphous (a-) SiCx, as determined by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). Annealing in vacuum up to 1450 °C resulted in improved crystallinity and a decreased volume fraction of the amorphous phase. Additionally, differential scanning calorimetry (DSC) was used to monitor heat flows connected to the respective reactions in the material, where a broad exothermic peak attributed to grain growth of crystalline TiCx appeared, while an exothermic reaction related to the formation of Ti3SiC2 was not detected. Tribological testing in a ball-on-disk setup was conducted at room temperature, 500 and 700 °C against an alumina counterpart. The room temperature measurement resulted in a coefficient of friction value of 0.8, at elevated temperatures the coefficient of friction decreased to 0.4. © 2006 Elsevier B.V. All rights reserved.
Nyckelord
- NATURAL SCIENCES
- NATURVETENSKAP
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Rester, M.
-
Neidhardt, Jörg, ...
-
Eklund, Per, 197 ...
-
Emmerlich, Jens, ...
-
Ljungcrantz, H.
-
Hultman, Lars, 1 ...
-
visa fler...
-
Mitterer, C.
-
visa färre...
- Artiklar i publikationen
-
Materials Scienc ...
- Av lärosätet
-
Linköpings universitet