- Nguyen, Son Tien, 1953- (författare)
- Linköpings universitet,Tekniska högskolan,Halvledarmaterial
-
- Chen, Weimin, 1959- (författare)
- Linköpings universitet,Tekniska högskolan,Funktionella elektroniska material
-
Lindström, J. L. (författare)
-
visa fler...
-
- Monemar, Bo, 1942- (författare)
- Linköpings universitet,Tekniska högskolan,Halvledarmaterial
-
- Janzén, Erik, 1954- (författare)
- Linköpings universitet,Tekniska högskolan,Halvledarmaterial
-
visa färre...
-
(creator_code:org_t)
- 1999
- 1999
- Engelska.
-
Ingår i: Physica Scripta. - 0031-8949 .- 1402-4896. ; T79, s. 46-49
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Electron paramagnetic resonance (EPR) was used to study defects in 4H and 6H SiC irradiated with 2.5 MeV electrons at room temperature. When the dose of irradiation reaches ~ 5 × 1017 electrons/cm2, an EPR spectrum appears. In both 4H and 6H SiC, the defect associated with this spectrum has C1h symmetry with an effective electron spin S = 1 and an isotropic g-value of 2.0063 ± 0.0002. The crystal-field parameter was determined as D = 1.65 and D = 1.67 GHz for 4H and 6H SiC, respectively. The principal crystal-field axis lies in the (11bar 20) plane and makes an angle of ~ 46° with the c-axis for both polytypes. A clear hyperfine structure from 29Si due to the interaction with four nearest silicon neighbours was observed, confirming that the defect is related to the carbon vacancy. The similarity in all respects including the annealing behaviour of the spectrum in both polytypes suggests that it belongs to the same defect. Based on the formation and its electronic structure, the defect is suggested to be a complex with one of the components being the carbon vacancy.