Dense single-phase β-sialon ceramics by glass-encapsulated hot isostatic pressing
-
- Ekström, Thommy (författare)
- AB Sandvik Hard Materials, Stockholm
-
- Käll, Per-Olov (författare)
- University of Stockholm
-
- Nygren, Mats (författare)
- University of Stockholm
-
visa fler...
-
- Olsson, Per-Olof (författare)
- University of Stockholm
-
visa färre...
-
(creator_code:org_t)
- 1989
- 1989
- Engelska.
-
Ingår i: Journal of Materials Science. - 0022-2461. ; 24:5, s. 1853-1861
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Single phase-sialon ceramics, Si6–z Al z O z N8–z , have been prepared from carefully balanced powder mixtures, also taking account of any excess oxygen in the starting materials. Sintering powder compacts in a nitrogen atmosphere (0.1 MPa) at 1800° C or higher transforms the starting mixture into a-sialon solid solution atz-values up to about 4.3, but the sintered material has an open porosity. Addition of 1 wt% Y2O3 to the starting mix improved the sintering behaviour somewhat and the density of the sintered compacts reached 95% of the theoretical value. By glass-encapsulated hot isostatic pressing at 1825° C, however, sintered materials of virtually theoretical density could be obtained, with or without the 1 wt% Y2O3 addition. These latter samples have been studied by X-ray diffraction and electron microscopy, and their hardness and indentation fracture toughness have been measured. It was found that the maximum extension of the-sialon phase composition at 1825° C and 200 MPa pressure is slightly below 4,z 3.85 and about 4.1 at atmospheric pressure, and that the hexagonal unit cell parameters are linear functions of thez-value. The single-phase-sialon ceramics had no residual glassy grain-boundary phase. The grain shape was equi-axed and the grain size increased from about 1m at lowz-values to 5m at highz-values. At lowz-values the hardness at a 98 N load was 1700 and the fracture toughness 3, whereas an increase inz above 1 caused both the hardness and fracture toughness to decrease significantly. Addition of 1 wt % Y2O3 to the starting mix prior to the HIP-sintering gave rise to a small amount of amorphous intergranular phase, changes in grain size and shape, a clear increase in fracture toughness and a moderate decrease in hardness.