Thermal stability and mechanical properties of arc evaporated ZrN/ZrAlN multilayers
-
- Rogström, Lina (författare)
- Linköpings universitet,Nanostrukturerade material,Tekniska högskolan
-
- Johnson, Lars (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska högskolan
-
- Johansson, Mats (författare)
- SECO Tools AB, Fagersta
-
visa fler...
-
- Ahlgren, Mats (författare)
- Sandvik Tooling AB, Stockholm
-
- Hultman, Lars (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska högskolan,Thin Film Physics
-
- Odén, Magnus (författare)
- Linköpings universitet,Nanostrukturerade material,Tekniska högskolan
-
visa färre...
-
(creator_code:org_t)
- Elsevier, 2010
- 2010
- Engelska.
-
Ingår i: Thin Solid Films. - : Elsevier. - 0040-6090 .- 1879-2731. ; 519:2, s. 694-699
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- ZrN1.20/Zr0.44Al0.56N1.20 multilayer films as well as ZrN1.17 and Zr0.44Al0.56N1.20 films were deposited by reactive arc evaporation on WC–Co substrates. Samples were post-deposition annealed for 2 h at 800–1200 °C. As-deposited and heat treated films were characterized by scanning transmission electron microscopy, X-ray diffraction and nanoindentation. The thermal stability was studied using a combination of differential scanning calorimetry, thermogravimetry, and mass spectrometry. The as-deposited Zr0.44Al0.56N1.20 film exhibits a nanocomposite structure of cubic and wurtzite ZrAlN. During annealing, the formation of ZrN- and AlN-rich domains results in age hardening of both the Zr0.44Al0.56N1.20 and the ZrN/ZrAlN multilayers. The age hardening is enhanced in the ZrN/ZrAlN multilayer due to straining of the ZrAlN sublayers in which a maximum hardness of 31 GPa is obtained after annealing at 1100 °C.
Nyckelord
- Thin films; Zr-Al-N; Multilayer; Arc evaporation; TEM; Hardness