Composition tunable Al1-xInxN nanorod arrays grown by ultra-high-vacuum magnetron sputter epitaxy
-
- Hsiao, Ching-Lien (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska högskolan
-
- Palisaitis, Justinas (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska högskolan
-
- Junaid, Muhammad (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska högskolan
-
visa fler...
-
- Chen, Ruei-San (författare)
- Linköpings universitet,Institutionen för fysik, kemi och biologi,Tekniska högskolan
-
- Persson, Per O.Å. (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska högskolan
-
- Sandström, Per (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska högskolan
-
- Holtz, Per-Olof (författare)
- Linköpings universitet,Halvledarmaterial,Tekniska högskolan
-
- Hultman, Lars (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska högskolan
-
- Birch, Jens (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska högskolan
-
visa färre...
-
(creator_code:org_t)
- 2011
- Engelska.
- Relaterad länk:
-
https://urn.kb.se/re...
Abstract
Ämnesord
Stäng
- Self-assembled ternary Al1-xInxN nanorod arrays with variable In concentration, 0.10 ≤ x ≤ 0.32 have been realized onto c-plane sapphire substrates by ultra-high-vacuum magnetron sputter epitaxy with Ti0.21Zr0.79N or VN seed layers assistance. The formation of nanorods was very sensitive to the applied seed layer. Without proper seed layer assistance a continuous Al1-xInxN film was grown. The nanorods exhibit hexagonal crosssections with preferential growth along the c axis. A coaxial rod structure with higher In concentration in the core was observed by (scanning) transmission electron microscopy in combination with low-loss electron energy loss spectroscopy and energy dispersive xray spectroscopy. 5 K cathodoluminescence spectroscopy of Al0.86In0.14N nanorods revealed band edge emission at ~5.46 eV, which was accompanied by a strong defectrelated emission at ~ 3.38 eV.