Silica nanofibers based impedance type humidity detector prepared on glass substrate
-
- Batool, S S (författare)
- Linköpings universitet,Institutionen för teknik och naturvetenskap,Tekniska högskolan
-
- Imran, Z (författare)
- Linköpings universitet,Institutionen för teknik och naturvetenskap,Tekniska högskolan,Pakistan Inst. Engn. and Appl Sci, Pakistan
-
- Israr Qadir, Muhammad (författare)
- Linköpings universitet,Institutionen för teknik och naturvetenskap,Tekniska högskolan
-
visa fler...
-
- Jamil Rana, Sadaf (författare)
- Linköpings universitet,Institutionen för teknik och naturvetenskap,Tekniska högskolan
-
- Usman, M (författare)
- Pakistan Institute Engn and Appl Science, Pakistan
-
- Jamil, H (författare)
- Pakistan Institute Engn and Appl Science, Pakistan
-
- Rafiq, M A (författare)
- Pakistan Institute Engn and Appl Science, Pakistan
-
- Hasan, M M (författare)
- Pakistan Institute Engn and Appl Science, Pakistan
-
- Nur, Omer (författare)
- Linköpings universitet,Fysik och elektroteknik,Tekniska högskolan
-
- Willander, Magnus (författare)
- Linköpings universitet,Fysik och elektroteknik,Tekniska högskolan
-
visa färre...
-
(creator_code:org_t)
- Elsevier, 2013
- 2013
- Engelska.
-
Ingår i: Vacuum. - : Elsevier. - 0042-207X .- 1879-2715. ; 87, s. 1-6
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Impedance type relative humidity detector is fabricated by depositing electrospun silica nanofibers on glass substrate. The silica nanofibers with an average diameter similar to 150 nm and length similar to 100 mu m were used. Thermogravimetric and differential scanning calorimetric analysis confirm that the accurate annealing temperature is 500 degrees C for complete removal of PVP. Humidity detecting devices were fabricated by defining titanium electrodes on top of the silica nanofibers. The performance of silica nanofibers humidity detectors was tested by AC electrical measurements at 40-90% relative humidity. The response and the recovery times were 5 s and 3 s, respectively, between 40% and 90% relative humidity. Contribution of dipoles, space charge polarization, relaxation of these dipoles and low frequency dispersion phenomenon were observed during impedance measurements.
Nyckelord
- SiO2 nanofibers
- Electric modulus
- Humidity detector
- Response time
- TECHNOLOGY
- TEKNIKVETENSKAP
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
-
Vacuum
(Sök värdpublikationen i LIBRIS)
Till lärosätets databas
- Av författaren/redakt...
-
Batool, S S
-
Imran, Z
-
Israr Qadir, Muh ...
-
Jamil Rana, Sada ...
-
Usman, M
-
Jamil, H
-
visa fler...
-
Rafiq, M A
-
Hasan, M M
-
Nur, Omer
-
Willander, Magnu ...
-
visa färre...
- Artiklar i publikationen
-
Vacuum
- Av lärosätet
-
Linköpings universitet