Mechanism of hopping conduction in Be-Fe-Al-Te-O semiconducting glasses and glass-ceramics
-
- Wójcik, Natalia A. (författare)
- Linnéuniversitetet,Institutionen för byggd miljö och energiteknik (BET),Gdańsk University of Technology, Poland
-
- Tagiara, Nagia S. (författare)
- National Hellenic Research Foundation, Greece
-
- Möncke, Doris (författare)
- National Hellenic Research Foundation, Greece;Alfred University, USA
-
visa fler...
-
- Kamitsos, Efstratios, I (författare)
- National Hellenic Research Foundation, Greece
-
- Ali, Sharafat, Associate Professor, 1976- (författare)
- Linnéuniversitetet,Institutionen för byggd miljö och energiteknik (BET),Avancerade material
-
- Ryl, Jacek (författare)
- Gdańsk University of Technology, Poland
-
- Barczynski, Ryszard J. (författare)
- Gdańsk University of Technology, Poland
-
visa färre...
-
(creator_code:org_t)
- 2022-01-09
- 2022
- Engelska.
-
Ingår i: Journal of Materials Science. - : Springer Nature. - 0022-2461 .- 1573-4803. ; 57, s. 1633-1647
- Relaterad länk:
-
https://doi.org/10.1...
-
visa fler...
-
https://link.springe...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Electrical properties of beryllium-alumino-tellurite glasses and glass-ceramics doped with iron ions were studied using impedance spectroscopy. The conductivity was measured over a wide frequency range from 10 mHz to 1 MHz and the temperature range from 213 to 473 K. The D.C. conductivity values showed a correlation with the Fe-ion concentration and ratio of iron ions on different valence states in the samples. On the basis of Jonscher universal dielectric response the temperature dependence of conductivity parameters were determined and compared to theoretical models collected by Elliott. In glasses, the conduction process was found to be due to the overlap polaron tunneling while in glass-ceramics the quantum mechanical tunneling between semiconducting crystallites of iron oxides is proposed. The D.C. conductivity was found not to follow Arrhenius relation. The Schnakenberg model was used to analyze the conductivity behavior and the polaron hopping energy and disorder energy were estimated. Additionally, the correlation between alumina dissolution and basicity of the melts was observed.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Keramteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Ceramics (hsv//eng)
Nyckelord
- Glasteknologi
- Glass Technology
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas