Effect of open assembly time and equilibrium moisture content on the penetration of polyurethane adhesive into thermally modified wood
-
- Bastani, Alireza (författare)
- University of Göttingen, Germany
-
- Adamopoulos, Stergios (författare)
- Linnéuniversitetet,Institutionen för skog och träteknik (SOT),GoFP
-
- Militz, Holger (författare)
- University of Göttingen, Germany
-
(creator_code:org_t)
- 2015-12-17
- 2017
- Engelska.
-
Ingår i: The journal of adhesion. - : Taylor & Francis. - 0021-8464 .- 1563-518X .- 1545-5823. ; 93:7, s. 575-583
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The effect of wood moisture content and open assembly time on penetration of polyurethane (PU) adhesive into thermally treated Scots pine (195 and 210°C) was investigated according to effective (EP) and maximum penetration (MP) measurements using fluorescence microscopy. For samples treated at 195°C, a higher EP was noted at 8.6% equilibrium moisture content (EMC) after both assembly times (15 and 30 min) while for samples treated at 210°C, increasing wood moisture content resulted in a significant decrease in EP at 12.5% EMC after 15 min assembly time. Extending open assembly time was found to increase the EP of PU adhesive only in the case of samples treated at 195°C and with 8.6% EMC. For samples treated at both treatment temperatures and after shorter open assembly time, the highest MP observed at moderate EMC levels of 8.6 and 8.2% and the lowest at the higher EMC levels of 13.2 and 12.5%.
Ämnesord
- LANTBRUKSVETENSKAPER -- Lantbruksvetenskap, skogsbruk och fiske -- Trävetenskap (hsv//swe)
- AGRICULTURAL SCIENCES -- Agriculture, Forestry and Fisheries -- Wood Science (hsv//eng)
Nyckelord
- adhesive bondlines
- adhesive penetration
- bonding variables
- fluorescence microscopy
- polyurethanes
- thermal modification
- wood
- Forestry and Wood Technology
- Skog och träteknik
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas