Biochar reinforced PLA composite for fused deposition modelling (FDM): A parametric study on mechanical performance
- Artikel/kapitelEngelska2023
Förlag, utgivningsår, omfång ...
-
Elsevier B.V.2023
-
electronicrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:ltu-101626
-
https://urn.kb.se/resolve?urn=urn:nbn:se:ltu:diva-101626URI
-
https://doi.org/10.1016/j.jcomc.2023.100406DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
Validerad;2023;Nivå 2;2023-10-11 (joosat);CC BY 4.0 License
-
Rice husk biochar was added to polylactic acid (PLA) to create a biocomposite filament suitable for the extrusion-based 3D printing process of fused deposition modelling (FDM). Taguchi L16 was used for experiment design, and the significance of process parameters was determined using variance analysis (ANOVA). For a 0.3-mm layer thickness, the addition of 5 wt.% biochar resulted in ultimate tensile strength and a modulus of elasticity of 36 MPa and 1103 MPa, respectively. The addition of biochar had a negative influence on flexural strength. The maximum flexural modulus was obtained with 3 % biochar, 100 % infill density, and 0.1 mm layer thickness. Particularly, 1 % biochar resulted in a considerable increase in impact strength, while a subsequent rise in biochar resulted in a decrease, probably due to the agglomeration effect. For 3D printed neat PLA, the average tensile strength, tensile modulus, flexural strength, flexural modulus, and impact strength observed were 19 MPa, 550 MPa, 54 MPa, 1981 MPa, and 25 KJ/m2, respectively. Additionally, considering the output of each test, a multicriteria decision-making model, namely, TOPSIS, has been utilized for ranking the mechanical performance. In order to optimise the mechanical properties of three-dimensional printed objects, the study suggests a layer thickness of 0.2 mm, an infill density of 100 %, and raster angle of 0° as the FDM process parameters.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Kulkarni, AtulDepartment of Mechanical Engineering, Vishwakarma Institute of Information Technology, Pune 411046, India
(författare)
-
Munde, YashwantDepartment of Mechanical Engineering, Cummins College of Engineering for Women, Pune 411052, India
(författare)
-
Shinde, AvinashDepartment of Mechanical Engineering, Cummins College of Engineering for Women, Pune 411052, India
(författare)
-
Das, OisikLuleå tekniska universitet,Byggkonstruktion och brand(Swepub:ltu)oisdas
(författare)
-
Department of Mechanical Engineering, Vishwakarma Institute of Information Technology, Pune 411046, IndiaDepartment of Mechanical Engineering, Cummins College of Engineering for Women, Pune 411052, India
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Composites Part C: Open Access: Elsevier B.V.122666-6820
Internetlänk
Hitta via bibliotek
Till lärosätets databas