Influence of mineralogy on the hydraulic properties of ladle slag
-
- Adolfsson, Daniel (författare)
- SSAB Merox SE-61380 Oxelösund, Sweden
-
- Robinson, Ryan (författare)
- Luleå tekniska universitet,Institutionen för samhällsbyggnad och naturresurser
-
- Engström, Fredrik (författare)
- Luleå tekniska universitet,Industriell miljö- och processteknik
-
visa fler...
-
- Björkman, Bo (författare)
- Luleå tekniska universitet,Industriell miljö- och processteknik
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2011
- 2011
- Engelska.
-
Ingår i: Cement and Concrete Research. - : Elsevier BV. - 0008-8846 .- 1873-3948. ; 41:8, s. 865-871
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The present study is aimed at investigating the hydraulic characteristics of ladle furnace slag (LFS), under the pretence of using LFS as a cement substitute in certain applications. Furthermore, LFS has been considered as a possible activator in a blend containing 50% LFS, and 50% ground granulated blast furnace slag (GGBFS). Phases detected in LFS were quantified using Rietveld analysis. Calorimetric studies were performed at 20, 25 and 30 °C in order to calculate the apparent activation energy of hydration and thereby to suggest a kinetic model for the tested compositions within this temperature interval. In addition, compressive strength tests were performed on mortar prisms made with LFS, and LFS/GGBFS which had hydrated for 2, 7 and 28 days. Both compositions reached acceptable early strengths, (e.g. LFS, 33.1 MPa, and LFS/GGBFS, 17.9 MPa, after 2 days), but after 28 days hydration the blend was superior to neat LFS. Related apparent activation energies were determined using an Avrami–Erofeev model and gave Ea = 58 kJ/mol for neat LFS and Ea = 63 kJ/mol for the blend. The results imply that LFS or a LFS/GGBFS blend can be favourably used as supplement in binder applications such as binder in by-product metallurgical briquettes, which are used as recycle to the blast furnace or basic oxygen furnace depending on the specific briquette composition.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- Calcium aluminate cement (D)
- Calorimetry (A)
- Hydration (A)
- Ladle furnace slag
- Process Metallurgy
- Processmetallurgi
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas