Cu valence states in superconducting BiPbSrCaCuO system
-
- Liu, H.K. (författare)
- School of Materials Science and Engineering, University of New South Wales
-
- Dou, S.X. (författare)
- School of Materials Science and Engineering, University of New South Wales
-
- Song, K-H (författare)
- School of Materials Science and Engineering, University of New South Wales
-
visa fler...
-
- Sorrell, C.C. (författare)
- School of Materials Science and Engineering, University of New South Wales
-
- Easterling, Kenneth E. (författare)
- Luleå tekniska universitet
-
- Jones, W.K. (författare)
- College of Engineering and Applied Science, State University of Florida at Miami
-
visa färre...
-
(creator_code:org_t)
- 1990
- 1990
- Svenska.
-
Ingår i: Journal of Solid State Chemistry. - 0022-4596 .- 1095-726X. ; 87:2, s. 289-297
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The oxidation states of Bi, Pb, and Cu in the BiPbSrCaCuO (BPSCCO) system have been determined by a combination of volumetric measurement technique and iodometric titration. It was found that, in contrast to previous reports, the concentration of the Cu3+ ions decreased with increasing Pb content, and Cu3+ ions were absent in samples of Bi1.6Pb0.4Sr1.6Ca2Cu3O9.8, while a Tc at 108 K and a Jc of greater than 12,000 A/cm2 at 77 K were observed. The 110 K phase in BPSCCO was stabilized and showed a high tolerance to change in oxygen partial pressure during sintering. In Pb-doped materials, Bi appears to be trivalent while Pb was determined to be mixed-valence Pb4+ Pb2+. It is suggested that superconductivity in BPSCCO may result from a dynamic transfer of holes from Bi PbO layers toward CuO2 planes
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
Nyckelord
- Materialteknik
- Engineering Materials
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas