Andersons, J.Institute of Polymer Mechanics, University of Latvia, 23 Aizkraukles iela, LV-1006 Rīga, Latvia
(författare)
Prediction of crack onset strain in composite laminates at mixed mode cracking
- Artikel/kapitelEngelska2009
Förlag, utgivningsår, omfång ...
-
Bristol :IOP Publishing Ltd,2009
-
electronicrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:ltu-39837
-
https://urn.kb.se/resolve?urn=urn:nbn:se:ltu:diva-39837URI
-
https://doi.org/10.1088/1757-899X/5/1/012018DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:kon swepub-publicationtype
Anmärkningar
-
Validerad; 2009; 20091001 (ysko)
-
Failure process of continuous fiber reinforced composite laminates in tension usually starts with appearance of intralaminar cracks. In composite laminates with complex lay-ups and/or under combined loading, intralaminar cracks may develop in plies with different reinforcement directions. A necessary part of mixed mode cracking models is the criterion of failure. For propagation-controlled fracture it is usually formulated in terms of energy release rates and their critical values of the particular composite material. Intralaminar fracture toughness of unidirectionally reinforced glass/epoxy composite was experimentally determined at several mode I and mode II ratios. It is found that the crack propagation criterion, linear in terms of the energy release rates, reasonably well approximates the test results. The determined mixed mode cracking criterion was applied to predict intralaminar crack onset in cross-ply glass/epoxy composite under tensile loading. The predicted crack onset strain values agree with test results at small off-axes angles of the cracking ply (on-axis and 15° off-axis loading), but underestimate crack onset at larger reinforcement angles with respect to the loading direction. The discrepancy is likely to be caused by the deviation of linearity in laminate response before cracking onset in these laminates, related to non-linear shear characteristics of unidirectional plies. The applicability of strength-based fracture criterion for initiation-controlled cracking is discussed.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Sparnins, EdgarsLuleå tekniska universitet,Institute of Polymer Mechanics, University of Latvia, 23 Aizkraukles iela, LV-1006 Rīga, Latvia(Swepub:ltu)edgspa
(författare)
-
Joffe, RobertsLuleå tekniska universitet,Materialvetenskap(Swepub:ltu)joffe
(författare)
-
Luleå tekniska universitetInstitute of Polymer Mechanics, University of Latvia, 23 Aizkraukles iela, LV-1006 Rīga, Latvia
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:5th International EEIGM/AMASE/FORGEMAT Conference on Advanced Materials ResearchBristol : IOP Publishing Ltd
Internetlänk