Preparation for TEM of layered samples with fragile microstructure and weak layer interface
-
- Westman, Anna-Karin (författare)
- Luleå tekniska universitet,Träteknik,Luleå University of Technology
-
- Wei, Liu-Ying (författare)
- Luleå tekniska universitet,Luleå University of Technology
-
- Barre, F. (författare)
- Luleå tekniska universitet,Luleå University of Technology
-
(creator_code:org_t)
- 1999
- 1999
- Engelska.
-
Ingår i: Microscopy research and technique (Print). - 1059-910X .- 1097-0029. ; 45:3, s. 198-202
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- The objective of this work was to prepare for transmission electron microscopy (TEM) a layered structure of materials with fragile microstructure. The samples consisted of two layers of different materials, silicon nitride and borosilicate glass, loosely bonded together. The low strength of the sample resulted in fragmentation during more conventional preparation. However, it was possible to prepare the fragments by mounting them in a titanium specimen carrier with aluminium strips as support. After grinding and polishing, a technique of low-angle ion milling was used to obtain electron beam transparent areas at the nitride/glass interface.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Maskinteknik -- Annan maskinteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Mechanical Engineering -- Other Mechanical Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
Nyckelord
- Wood Technology
- Träteknik
- Engineering Materials
- Materialteknik
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas