Abdullha, Khalid A.Department of Civil Engineering, College of Engineering, Mosul University, Mosul, Iraq
(författare)
Mechanical properties, thermal and chemical effect of polymer cotton bars reinforced with carbon / glass fiber
- Artikel/kapitelEngelska2024
Förlag, utgivningsår, omfång ...
-
2022-09-25
-
Taylor & Francis,2024
-
electronicrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:ltu-93243
-
https://urn.kb.se/resolve?urn=urn:nbn:se:ltu:diva-93243URI
-
https://doi.org/10.1080/14484846.2022.2125472DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
Validerad;2024;Nivå 1;2024-06-27 (hanlid);Full text license: CC BY-NC-ND
-
Many researchers are interested in using natural fibres to treat due to recent advancements in polymer characteristics. The mechanical properties of three types of bars are studied in this paper: Cotton Fibre-Reinforced Polymer bars, Cotton/Carbon Fibre-Reinforced Polymer bars, and Cotton/Glass Fibre-Reinforced Polymer bars. The goal of the paper was to create low-cost bars with comparable mechanical performance and corrosion resistance to steel reinforcement. The bars were made using two methods: fibres immersed in polymer and fibres coated with polymer by repeated tension and relaxation of fibres. The second method produced better results in terms of the tensile strength of Cot.CFRP, Cot.GFRP, and Cot.FRP bars, which were 688, 477, and 284 MPa, respectively, and the stress–strain curve revealed brittle behaviour for all bars and modulus of elasticity of 43, 31 and 22 GPa. When sand was put on the bar’s surface, the bars demonstrated a good connection with the concrete. It also showed good resistance to moisture, alkaline solutions and acids, as well as heat resistance at temperatures below 200°C.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Abdullha, Aziz I.Department of Civil Engineering, College of Engineering, Tikrit University, Tikrit, Iraq
(författare)
-
Abdul-Razzak, Ayad A.Department of Civil Engineering, College of Engineering, Mosul University, Mosul, Iraq
(författare)
-
Al-Gburi, MajidLuleå tekniska universitet,Byggkonstruktion och brand(Swepub:ltu)majali
(författare)
-
Department of Civil Engineering, College of Engineering, Mosul University, Mosul, IraqDepartment of Civil Engineering, College of Engineering, Tikrit University, Tikrit, Iraq
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Australian Journal of Mechanical Engineering: Taylor & Francis22:3, s. 592-6021448-48462204-2253
Internetlänk
Hitta via bibliotek
Till lärosätets databas