Laser-assisted reduction of iron ore using aluminum powder
-
- Fedina, Tatiana (författare)
- Luleå tekniska universitet,Produkt- och produktionsutveckling
-
- Brueckner, Frank (författare)
- Luleå tekniska universitet,Produkt- och produktionsutveckling,Fraunhofer IWS, Winterbergstrasse 28, 01277 Dresden, Germany
-
- Kaplan, Alexander F. H. (författare)
- Luleå tekniska universitet,Produkt- och produktionsutveckling
-
visa fler...
-
- Wilsnack, Christoph (författare)
- Fraunhofer IWS, Winterbergstrasse 28, 01277 Dresden, Germany
-
visa färre...
-
(creator_code:org_t)
- American Institute of Physics (AIP), 2023
- 2023
- Engelska.
-
Ingår i: Journal of laser applications. - : American Institute of Physics (AIP). - 1042-346X .- 1938-1387. ; 35:2
- Relaterad länk:
-
https://doi.org/10.2...
-
visa fler...
-
https://ltu.diva-por... (primary) (Raw object)
-
https://urn.kb.se/re...
-
https://doi.org/10.2...
-
visa färre...
Abstract
Ämnesord
Stäng
- This study reports on the laser-assisted reduction of iron ore waste using Al powder as areducing agent. Due to climate change and the global warming situation, it has become ofparamount importance to search for and/or develop green and sustainable processes for ironand steel production. In this regard, a new method for iron ore utilization is proposed in thiswork, investigating the possibility of iron ore waste reduction via metallothermic reaction withAl powder. Laser processing of iron ore fines was performed, focusing on the Fe2O3-Alinteraction behavior and extent of the iron ore reduction. The reaction between the materialsproceeded in a rather intense uncontrolled manner which led to a formation of Fe-rich domainsand alumina as two separate phases. In addition, a combination of Al2O3 and Fe2O3 melts aswell as transitional areas such as intermetallics were observed, suggesting the occurrence ofincomplete reduction reaction in isolated regions. The reduced iron droplets were prone toacquire a sphere-like shape and concentrated mainly near the surface of the Al2O3 melt or at theinterface with the iron oxide. Both SEM, EDS and WDS analyses were employed to analyzechemical composition, microstructure and morphological appearances of the reaction products.High-speed imaging was used to study the process phenomena and observe differences in themovement behavior of the particles. Furthermore, the measurements acquired from X-raycomputed microtomography revealed that approximately 2.4 % of iron was reduced during thelaser processing of Fe2O3-Al powder bed, most likely due to insufficient reaction time orinappropriate equivalence ratio of the two components.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
Nyckelord
- iron ore
- aluminum
- reduction
- sustainability
- laser powder bed fusion
- additive manufacturing
- Produktionsutveckling
- Manufacturing Systems Engineering
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas