High-speed X-ray study of process dynamics caused by surface features during continuous-wave laser polishing
-
- Faue, Patrick (författare)
- Department of Mechanical Engineering, University of Wisconsin-Madison, Madison, WI 53706 USA
-
- Rathmann, Lewin (författare)
- Bremer Institut für angewandte Strahltechnik GmbH, Bremen 28359, Germany
-
- Möller, Marius (författare)
- Bremer Institut für angewandte Strahltechnik GmbH, Bremen 28359, Germany
-
visa fler...
-
- Hassan, Mahmudul (författare)
- Department of Mechanical Engineering, University of Wisconsin-Madison, Madison, WI 53706 USA
-
- Clark, Samuel J. (författare)
- X-ray Science Division, Advanced Photon Source, Argonne National Laboratory, Lemont, IL 60439, USA
-
- Fezzaa, Kamel (författare)
- X-ray Science Division, Advanced Photon Source, Argonne National Laboratory, Lemont, IL 60439, USA
-
- Klingbeil, Kevin (författare)
- Cross Product Solutions, LLC, Osceola, WI 54020, USA
-
- Richter, Brodan (författare)
- Department of Mechanical Engineering, University of Wisconsin-Madison, Madison, WI 53706 USA
-
- Volpp, Joerg (författare)
- Luleå tekniska universitet,Produkt- och produktionsutveckling
-
- Radel, Tim (författare)
- Bremer Institut für angewandte Strahltechnik GmbH, Bremen 28359, Germany
-
- Pfefferkorn, Frank E. (författare)
- Department of Mechanical Engineering, University of Wisconsin-Madison, Madison, WI 53706 USA
-
visa färre...
-
(creator_code:org_t)
- Elsevier, 2023
- 2023
- Engelska.
-
Ingår i: CIRP annals. - : Elsevier. - 0007-8506 .- 1726-0604. ; 72:1, s. 201-204
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- During high-speed X-ray imaging of laser surface polishing experiments of specimens of 316L stainless steel at Argonne National Lab's Advanced Photon Source, it was discovered that the induced keyhole changes shape and dimensions while crossing an engineered surface feature without altering process parameters. It was observed that the post-surface feature keyhole was deeper than that of the pre surface feature keyhole. This work reports on the first in-situ observation of the effect of localized surface geometry on underlying melt pool behavior. This has implications for defect formation mechanisms during laser melting processes that rely on melt pool geometry.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
Nyckelord
- Laser
- Polishing
- X-ray imaging
- Produktionsutveckling
- Manufacturing Systems Engineering
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Faue, Patrick
-
Rathmann, Lewin
-
Möller, Marius
-
Hassan, Mahmudul
-
Clark, Samuel J.
-
Fezzaa, Kamel
-
visa fler...
-
Klingbeil, Kevin
-
Richter, Brodan
-
Volpp, Joerg
-
Radel, Tim
-
Pfefferkorn, Fra ...
-
visa färre...
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Materialteknik
-
och Bearbetnings yt ...
- Artiklar i publikationen
-
CIRP annals
- Av lärosätet
-
Luleå tekniska universitet