Damage sequence in thin-ply composite laminates under out-of-plane loading
-
- Wagih, A. (författare)
- University of Girona, Spain; Zagazig University, Egypt
-
- Maimí, P. (författare)
- University of Girona, Spain
-
- González, E. V. (författare)
- University of Girona, Spain
-
visa fler...
-
- Blanco, N. (författare)
- University of Girona, Spain
-
- De Aja, J. R. S. (författare)
- Aernnova Engineering Solutions Ibérica S.A., Spain
-
- De La Escalera, F. M. (författare)
- Aernnova Engineering Solutions Ibérica S.A., Spain
-
- Olsson, Robin (författare)
- RISE,SICOMP
-
- Alvarez, E. (författare)
- Oxeon AB, Sweden
-
visa färre...
-
(creator_code:org_t)
- Elsevier Ltd, 2016
- 2016
- Engelska.
-
Ingår i: Composites. Part A, Applied science and manufacturing. - : Elsevier Ltd. - 1359-835X .- 1878-5840. ; 87, s. 66-77
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The study of the damage sequence in polymer-based composite laminates during an impact event is a difficult issue. The problem can be more complex when the plies are thin. In this paper, quasi-static indentation tests were conducted on thin-ply laminates to understand qualitatively the damage mechanisms and their sequence during low-velocity impact loading. TeXtreme® plain weave plies were used with two different thicknesses, 0.08 mm and 0.16 mm (referenced as ultra-thin-ply and thin-ply, respectively), and tested under different load levels. Load-displacement curves were analyzed and the extent of damage was inspected using optical microscopy and ultrasonic technique. The results showed that the damage onset occurs earlier in thin-ply laminates. The damage onset in thin-ply laminates is matrix cracking which induces delaminations, whereas for ultra-thin-ply laminates is due to delaminations which are induced by shear forces and small amount of matrix cracking. Moreover, the fiber breakage appears earlier in ultra-thin-ply laminates.
Nyckelord
- A. Polymer-matrix composites (PMCs)
- B. Impact behavior
- C. Damage mechanics
- D. Fractography
- Cracks
- Delamination
- Fracture mechanics
- Laminated composites
- Paper laminates
- Polymer matrix composites
- Ultrasonic applications
- Ultrasonic testing
- Damage mechanics
- Impact behavior
- Load-displacement curve
- Out-of-plane loading
- Polymer based composite
- Polymer Matrix Composites (PMCs)
- Quasi-static indentation tests
- Ultrasonic techniques
- Laminates
- Composites
- Damage
- Ply Wood
- Ultrasonic Frequencies
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas