Larsson, HenrikUmeå universitet,Kemiska institutionen
(författare)
Ellipsometric determinations of the thicknesses of dry and electrolyte-immersed poly(4-vinylpyridine) films containing coordinated light-absorbing [Os(bpy)2pvpCl]2+/+ redox groups
- Artikel/kapitelEngelska1994
Förlag, utgivningsår, omfång ...
-
Elsevier,1994
-
printrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:umu-112729
-
https://urn.kb.se/resolve?urn=urn:nbn:se:umu:diva-112729URI
-
https://doi.org/10.1016/0022-0728(93)02992-QDOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
Ellipsometry has been used to measure the dimensions of quaternized poly(4-vinylpyridine) films containing [Os(bpy)2pvpCl]2+/+ redox groups on glassy carbon electrodes. Film thicknesses and complex refractive indices were deduced using molar absorptivities obtained from photometry or a combination of photometry and cyclic voltammetry. The precision in the film thicknesses was estimated using data obtained from thick and thin films with the same polymer + redox group compositions and from data recorded at 60-degrees and 70-degrees angles of incidence of 633 nm laser light. The effects of errors in the experimentally determined molar absorptivity of the redox groups on film thickness were also assessed. The results of this study suggest that reliable thicknesses can be obtained for both dry and electrolyte-swollen films, and that the presence of light-absorbing redox groups within coatings such as these presents no real obstacle for ellipsometric determinations.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Umeå universitetKemiska institutionen
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Journal of Electroanalytical Chemistry: Elsevier365:1-2, s. 229-2371572-66571873-2569
Internetlänk
Hitta via bibliotek
Till lärosätets databas