Sökning: onr:"swepub:oai:DiVA.org:umu-11871" >
Electrical properti...
Electrical properties of 3D-polymeric crystalline and disordered C60 and C70 fullerites.
-
Buga, Sergei G. (författare)
-
Blank, Vladimir D. (författare)
-
Serebryanaya, Nadejda R. (författare)
-
visa fler...
-
- Dzwilewski, Andrzej (författare)
- Umeå universitet,Institutionen för fysik
-
- Makarova, Tatiana (författare)
- Umeå universitet,Institutionen för fysik
-
- Sundqvist, Bertil (författare)
- Umeå universitet,Institutionen för fysik
-
visa färre...
-
(creator_code:org_t)
- Elsevier B.V. 2005
- 2005
- Engelska.
-
Ingår i: Diamond and Related Materials vol. 14, special Issue (3-7). - : Elsevier B.V.. ; , s. 896-901
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Crystalline and disordered 3D-polymeric C60 and C70 with different lattice parameters and with densities in the range of 2.2÷3.25 g cm−1 were obtained by high-pressure-high-temperature treatment at P=11.5÷15 GPa, T=670÷1800 K. Their d.c. electrical conductivity was investigated at temperatures 30÷350 K. The variable range hopping mechanism dominates in all samples up to room temperature. A temperature activated conductivity via delocalized states was observed at T>160÷260 K in crystalline C60 samples and in some samples with disordered structure. The evaluated band gap value is Eg=0.28÷0.54 eV for different crystalline structures and 0.06÷0.25 eV for disordered ones
Ämnesord
- NATURVETENSKAP -- Fysik -- Den kondenserade materiens fysik (hsv//swe)
- NATURAL SCIENCES -- Physical Sciences -- Condensed Matter Physics (hsv//eng)
Nyckelord
- Fullerenes
- fullerene polymers
- C60
- C70
- lattice parameters
- high pressure
- high temperature
- synthesis
- electrical conductivity
- resistivity
- resistance
- electrical transport
- variable range hopping
- band gap
- Condensed matter physics
- Kondenserade materiens fysik