Highly Enhanced Luminescence from Single-Crystalline C60·1m-xylene Nanorods

Single-crystalline C60â1m-xylene nanorods with a hexagonal structure were successfully synthesizedby evaporating a C60 solution in m-xylene at room temperature. The ratio of the length to the diameterof the nanorods can be controlled in the range of 10 to over 1000 for different applications. Thephotoluminescence (PL) intensity of the nanorods is about 2 orders of magnitude higher than that forpristine C60 crystals in air. Both UV and Raman results indicate that there is no charge transfer betweenC60 and m-xylene. It was found that the interaction between C60 and m-xylene molecules is of the vander Waals type. This interaction reduces the icosahedral symmetry of C60 molecule and induces strongPL from the solvate nanorods.

Liu, Bingbing (författare)
Yu, Shidan (författare)
Yao, Mingguang (författare)
Liu, Dedi (författare)
Hou, Yuanyuan (författare)
Cui, Tian (författare)
Zou, Guangtian (författare)
Sundqvist, BertilUmeå universitet,Institutionen för fysik(Swepub:umu)besu0001 (författare)
You, Han (författare)
Zhang, Dingke (författare)
Ma, Dongge (författare)
Umeå universitetInstitutionen för fysik (creator_code:org_t)

Ingår i:Chemistry of Materials: American Chemical Society (ACS)18:17, s. 4190-41940897-47561520-5002

Av författaren/redakt...: Wang, Lin; Liu, Bingbing; Yu, Shidan; Yao, Mingguang; Liu, Dedi; Hou, Yuanyuan; visa fler...; Cui, Tian; Zou, Guangtian; Sundqvist, Berti ...; You, Han; Zhang, Dingke; Ma, Dongge; visa färre...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.