On wear resistance ...
On wear resistance of tool steel
-
- Broqvist, Natalia (författare)
- Uppsala universitet,Tillämpad materialvetenskap
-
- Hogmark, Sture (författare)
- Uppsala universitet,Tillämpad materialvetenskap
-
Medvedeva, A. (författare)
-
visa fler...
-
Gunnarsson, S. (författare)
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2012
- 2012
- Engelska.
-
Ingår i: Journal of Manufacturing Processes. - : Elsevier BV. - 1526-6125. ; 14:3, s. 195-198
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Maintaining a reasonably low cutting tool wear when producing forming tools is a general challenge in the development of new forming tool materials. The tool life of a hot forming tool steel (H13) has been significantly improved by reducing its Si-content from 1.0 to 0.06 wt.%. However, this modified H13 (MH13) also displays a reduced cutting tool life due to higher cutting forces and a stronger tendency to form built up layers (BUE) on the cutting edge. This paper explains why.Gleeble tests of MH13 revealed a significantly higher flow stress in the 820–900 °C temperature interval in MH13 compared to H13. Thermo-Calc simulations showed that when reducing the Si-content from 1.0 to 0.06 wt.% the initial temperature for ferrite-to-austenite transformation (A1) was reduced from 900 °C to 820 °C. Knowing that austenite has totally different mechanical and thermal properties than ferrite, the difference in A1 between the two steels explains the higher cutting forces and higher tendency for BUE-formation. The conclusion is that the difference in machinability between H13 and MH13 is primarily related to their difference in A1.An attempt was also made to find a new tool material composition that can combine the wear resistance of MH13 and the good machinability of H13. Thermo-Calc simulations were performed with slightly modified alloying content without changing its properties as a good forming tool material, with the aim to increase A1. For instance, reducing the Mn content from 0.5 to 0.05 wt.% proved to increase A1 from 820 to 850 °C.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
Nyckelord
- TECHNOLOGY
- TEKNIKVETENSKAP
- Teknisk fysik med inriktning mot materialvetenskap
- Engineering Science with specialization in Materials Science
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas