Abstract
Ämnesord
Stäng
- In this work we report the anodic formation of highly ordered nanoporous Ta2O5 layers that exhibit a self-ordered alignment of pores uniformly over the anodized surface. These layers are grown by anodization of tantalum in a nonaqueous electrolyte consisting of an optimized glycerol/ethylene glycol mixture with the addition of NH4F . To reach an optimized nanoporous structure, several factors [fluoride concentration and content of supporting electrolyte (NH4)2SO4 ] need to be controlled. Once optimized, the nanopore diameter can be adjusted using the applied voltage in the range of 7–18 nm, and layers with a thickness of more than 10μm can be grown. As a result, a pore aspect ratio of 1000 can be reached.
Ämnesord
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas