In Situ Coating of Flame-Made TiO2 Particles with Nanothin SiO2 Films
-
- Teleki, Alexandra (författare)
- ETH, Dept Mech & Proc Engn, Particle Technol Lab, CH-8092 Zurich, Switzerland.
-
- Heine, Martin C. (författare)
- ETH, Dept Mech & Proc Engn, Particle Technol Lab, CH-8092 Zurich, Switzerland.
-
- Krumeich, Frank (författare)
- ETH, Ctr Electron Microscopy EMEZ, CH-8092 Zurich, Switzerland.
-
visa fler...
-
- Akhtar, M. Kamal (författare)
- Millennium Inorgan Chem, Glen Burnie, MD 21060 USA.
-
- Pratsinis, Sotiris E. (författare)
- ETH, Dept Mech & Proc Engn, Particle Technol Lab, CH-8092 Zurich, Switzerland.
-
visa färre...
-
ETH, Dept Mech & Proc Engn, Particle Technol Lab, CH-8092 Zurich, Switzerland ETH, Ctr Electron Microscopy EMEZ, CH-8092 Zurich, Switzerland. (creator_code:org_t)
- 2008-10-11
- 2008
- Engelska.
-
Ingår i: Langmuir. - : American Chemical Society (ACS). - 0743-7463 .- 1520-5827. ; 24:21, s. 12553-12558
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Rutile TiO2 particles made by flame spray pyrolysis (FSP) were coated in a single step with SiO2 layers in an enclosed flame reactor. This in situ particle coating was accomplished by a hollow ring delivering hexamethyldisiloxane (HMDSO) vapor (precursor to SiO2) through multiple jets in swirl cross-flow to Al-doped nanostructured rutile TiO2 aerosol freshly made by FSP of a solution of titanium tetraisopropoxide and aluminum sec-butoxide in xylene. The as-prepared powders were characterized by (scanning) transmission electron microscopy (STEM and TEM), energy dispersive X-ray analysis, X-ray diffraction, nitrogen adsorption, electrophoretic mobility, DC plasma optical emission (DCP-OES), and Fourier transform infrared (FT-IR) spectroscopy. The coating quality was assessed further by the photocatalytic oxidation of isopropyl alcohol to acetone. The effect of HMDSO injection point and vapor concentration on product particle morphology was investigated. The titania particles were uniformly SiO2-coated with controlled and uniform thickness at a production rate of about 30 g h(-1) and exhibited limited, if any, photoactivity. In contrast, spraying and combusting equivalent mixtures of the above Si/Al/Ti precursors in the above reactor (without delivering HMDSO through the hollow ring) resulted in particles segregated in amorphous (SiO2) and crystalline (TiO2) domains which exhibited high photocatalytic activity.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Nanoteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Nano-technology (hsv//eng)
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
-
Langmuir
(Sök värdpublikationen i LIBRIS)
Till lärosätets databas