The quality of SiO(2)-coatings on flame-made TiO(2)-based nanoparticles
-
- Teleki, A. (författare)
- ETH, Dept Mech & Proc Engn, Particle Technol Lab, CH-8092 Zurich, Switzerland.
-
- Akhtar, M. K. (författare)
- Millennium Inorgan Chem Cristal Com, Res Ctr, Glen Burnie, MD 21060 USA.
-
- Pratsinis, S. E. (författare)
- ETH, Dept Mech & Proc Engn, Particle Technol Lab, CH-8092 Zurich, Switzerland.
-
ETH, Dept Mech & Proc Engn, Particle Technol Lab, CH-8092 Zurich, Switzerland Millennium Inorgan Chem Cristal Com, Res Ctr, Glen Burnie, MD 21060 USA. (creator_code:org_t)
- Royal Society of Chemistry (RSC), 2008
- 2008
- Engelska.
-
Ingår i: Journal of Materials Chemistry. - : Royal Society of Chemistry (RSC). - 0959-9428 .- 1364-5501. ; 18:30, s. 3547-3555
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Silica-coated titania nanoparticles are important in sunscreens, UV filters and optical nanocomposites. The surface characteristics (extent of coverage, texture and thickness) of in situ SiO(2)-coated, mostly rutile titania nanoparticles made in one step by flame spray pyrolysis (FSP) were compared to FSP-made mixed (co-oxidized) SiO(2)/TiO(2) ones by transmission electron microscopy (TEM), Raman, FT-IR spectroscopy, electrophoretic mobility and isopropanol chemisorption followed by mass spectroscopy. Increasing the silica content shifted the isoelectric point (IEP) toward that of pure silica for externally mixed SiO(2) and TiO(2), co-oxidized SiO(2)/TiO(2) and low SiO(2) content (< 10 wt%) silicacoated TiO(2) nanoparticles. At higher SiO(2) contents, SiO(2)-coated titania exhibited negative z potentials at all pH values (and thus no IEP) indicating hermetic or complete coverage of the TiO(2) surface by SiO(2) as was confirmed by isopropanol chemisorption. Co-oxidized particles containing segregated TiO(2) and SiO(2) domains exhibited Si-O-Ti and Si-O-Si bonds of higher IR intensity than hermetically-coated TiO(2). The latter exhibited a peak at 1225 cm(-1) attributed to Si-O-Si asymmetric vibrations in contrast to the former.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Nanoteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Nano-technology (hsv//eng)
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas