High-pressure liquid dispersion and fragmentation of flame-made silica agglomerates

• The influence of primary particle diameter and the degree of agglomeration of flame-made silica agglomerate suspensions in aqueous solutions is studied by high-pressure dispersion (up to 1500 bar) through a nozzle with a 125 Am inner diameter. These particles were produced (4-15 g/h) by oxidation of hexamethyldisiloxane (HMDSO) in a coflow diffusion flame reactor. Their average primary particle size (10-50 nm) and degree of agglomeration were controlled by varying the oxygen and precursor flow rates. The particles were characterized by nitrogen adsorption, electron microscopy, and small-angle X-ray scattering. Hydrodynamic stresses break up soft agglomerates and yield hard agglomerate sizes in the range of 100-180 nm, as characterized by dynamic light scattering. Soft agglomerates exhibited decreasing light scattering diameters with increasing dispersion pressure, while hard agglomerates were insensitive.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Nanoteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Nano-technology (hsv//eng)

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)