Effect of nitrogen vacancies on the growth, dislocation structure, and decomposition of single crystal epitaxial (Ti1-xAlx)N-y thin films

• The effect of varying nitrogen vacancies on the growth, microstructure, spinodal decomposition and hardness values of predominantly single crystal cubic phase c-(Ti1-xAlx)N-y films was investigated. Epitaxial c-(Ti1-xAlx)N-y films with y = 0.67, 0.79, and 0.92 were grown on MgO(001) and MgO(111) substrates by magnetron sputter deposition. High N vacancy c-(Ti1-xAlx)N-0.67 films deposited on MgO(111) contained coherently oriented w-(0001) structures while segregated conical structures were observed on the films grown on MgO(001). High resolution STEM images revealed that the N-deficient growth conditions induced segregation with small compositional fluctuations that increase with the number of N vacancies. Similarly, strain map analysis of the epitaxial c-(Ti1-xAlx)N-y (001) and (111) films show fluctuations in strain concentration that scales with the number of N vacancies and increases during annealing. The spinodal decomposition coarsening rate of the epitaxial c-(Ti1-xAlx)N-y films was observed to increase with decreasing N vacancies. Nanoindentation showed decreasing trends in hardness of the as-deposited films as the N vacancies increase. Isothermal post-anneal at 1100 degrees C in vacuum for 120 min revealed a continuation in the increase in hardness for the film with the largest number of N vacancies (y = 0.67) while the hardness decreased for the films with y = 0.79 and 0.92. These results suggest that nitrogen-deficient depositions of c-(Ti1-xAlx)N-y films help to promote a self-organized phase segregation, while higher N vacancies generally increase the coherency strain which delays the coarsening process and can influence the hardness at high temperatures.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

Nyckelord

Thin Films

Nitrogen vacancies

TiAlN system

spinodal decomposition

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)