Magnetron sputtering of carbon supersaturated tungsten films-A chemical approach to increase strength
-
- Fritze, Stefan (författare)
- Uppsala universitet,Oorganisk kemi
-
- Chen, M. (författare)
- Swiss Fed Inst Technol, Lab Nanomet, Vladimir Prelog Weg 5, CH-8093 Zurich, Switzerland.
-
- Riekehr, Lars (författare)
- Uppsala universitet,Institutionen för kemi - Ångström
-
visa fler...
-
- Osinger, Barbara (författare)
- Uppsala universitet,Oorganisk kemi
-
- Sortica, Mauricio A. (författare)
- Uppsala universitet,Tandemlaboratoriet
-
- Srinath, Aishwarya (författare)
- Uppsala universitet,Oorganisk kemi
-
- Menon, Ashok S. (författare)
- Uppsala universitet,Institutionen för kemi - Ångström
-
- Lewin, Erik, Dr. 1979- (författare)
- Uppsala universitet,Oorganisk kemi
-
- Primetzhofer, Daniel (författare)
- Uppsala universitet,Tandemlaboratoriet,Institutionen för fysik och astronomi
-
- Wheeler, J. M. (författare)
- Swiss Fed Inst Technol, Lab Nanomet, Vladimir Prelog Weg 5, CH-8093 Zurich, Switzerland.
-
- Jansson, Ulf, 1960- (författare)
- Uppsala universitet,Oorganisk kemi
-
visa färre...
-
(creator_code:org_t)
- Elsevier, 2021
- 2021
- Engelska.
-
Ingår i: Materials & design. - : Elsevier. - 0264-1275 .- 1873-4197. ; 208
- Relaterad länk:
-
https://doi.org/10.1...
-
visa fler...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Tungsten (W)-based materials attract significant attention due to their superior mechanical properties. Here, we present a chemical approach based on the addition of carbon (C) for increased strength via the combination of three strengthening mechanisms in W thin films. W:C thin films with C concentrations up to-4 at.% were deposited by magnetron sputtering. All films exhibit a body-centred-cubic structure with strong texture and columnar growth behaviour. X-ray and electron diffraction measurements suggest the formation of supersaturated W:C solid solution phases. The addition of C reduced the average column width from-133 nm for W to-20 nm for the film containing-4 at.% C. The column refinement is explained by a mechanism where C acts as re-nucleation sites. The W film is-13 GPa hard, while the W:C films achieve a peak hardness of-24 GPa. The W:C films are-11 GPa harder than the W film, which is explained by a combination of grain refinement strengthening, solid solution strengthening and increased dislocation density. Additional micropillar compression tests showed that the flow stress increased upon C addition, from-3.8 to-8.3 GPa and no brittle fracture was observed.
Ämnesord
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
Nyckelord
- Small-scale mechanical characterisation
- Tungsten
- PVD
- Supersaturated solid solution
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Fritze, Stefan
-
Chen, M.
-
Riekehr, Lars
-
Osinger, Barbara
-
Sortica, Maurici ...
-
Srinath, Aishwar ...
-
visa fler...
-
Menon, Ashok S.
-
Lewin, Erik, Dr. ...
-
Primetzhofer, Da ...
-
Wheeler, J. M.
-
Jansson, Ulf, 19 ...
-
visa färre...
- Om ämnet
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Kemi
-
och Materialkemi
- Artiklar i publikationen
-
Materials & desi ...
- Av lärosätet
-
Uppsala universitet