Gelatin-coated mesoporous forsterite scaffold for bone tissue engineering
-
- Mohagheghiyan, Kiana (författare)
- Isfahan Univ Technol, Dept Mat Engn, Esfahan 8415683111, Iran.
-
- Mokhtari, Hamidreza (författare)
- Uppsala universitet,Makromolekylär kemi
-
- Kharaziha, Mahshid (författare)
- Isfahan Univ Technol, Dept Mat Engn, Esfahan 8415683111, Iran.
-
Isfahan Univ Technol, Dept Mat Engn, Esfahan 8415683111, Iran Makromolekylär kemi (creator_code:org_t)
- Elsevier, 2024
- 2024
- Engelska.
-
Ingår i: Ceramics International. - : Elsevier. - 0272-8842 .- 1873-3956. ; 50:8, s. 13526-13535
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- This study aims to develop a mesoporous forsterite spheres-based scaffold for bone tissue regeneration. To achieve this goal, mesoporous forsterite spheres were fabricated using alginate (gel-forming agent) and activated charcoal (porogen). The impact of carbon concentration (2, 5, 10, and 20 wt %) and sintering temperature (1100 and 1200 °C) on the structural properties of mesoporous forsterite spheres was investigated. Additionally, gelatin coatings were applied to modify these spheres. Forsterite microspheres with a particle size of 2.43 ± 0.22 mm were successfully produced, exhibiting varying pore sizes based on the sintering temperature and carbon content. Notably, mesoporous forsterite spheres synthesized using 5 wt% carbon and sintered at 1200 °C displayed uniform morphology, a minor average diameter (2.4 ± 0.3 mm(, and an average pore size of 2.7 ± 0.9 μm. These optimized forsterite spheres exhibited mesoporous structures with superior surface area (2.93 m2g-1) and pore volume (0.009–0.048 cm3g-1). Furthermore, the gelatin coating, with an average thickness of 160 μm, was effectively applied to the forsterite spheres. The gelatin coating reduced the surface area (1.40 m2g-1), pore volume (0.003 cm3g-1), and average pore diameter to 9.26 nm, maintaining the mesoporous structure. Both mesoporous forsterite spheres successfully induced bone-like apatite formation in vitro during a 21-day immersion in simulated body fluid. Moreover, while both forsterite-based spheres exhibited cytocompatibility with MG63 cells (cell viability >80 %), the gelatin coating significantly enhanced osteogenic differentiation (1.29 times). In conclusion, gelatin-coated mesoporous forsterite spheres exhibit promising potential as bioactive filling scaffolds for bone tissue regeneration.
Ämnesord
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Medicinteknik -- Medicinsk material- och protesteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Medical Engineering -- Medical Materials (hsv//eng)
Nyckelord
- Forsterite
- Mesoporous sphere
- Bone tissue engineering scaffold
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas