Proton irradiation-induced cracking and microstructural defects in UN and (U,Zr)N composite fuels
-
- Charatsidou, Elina (författare)
- KTH Royal Inst Technol, Stockholm, Sweden.;KTH Royal Inst Technol, Corresponding author Phys Dept, Nucl Sci & Engn, S-10691 Stockholm, Sweden.
-
- Giamouridou, Maria (författare)
- KTH Royal Inst Technol, Stockholm, Sweden.
-
- Fazi, Andrea (författare)
- Chalmers Univ Technol, Gothenburg, Sweden.
-
visa fler...
-
- Nagy, Gyula (författare)
- Uppsala universitet,Materialfysik
-
- Ribeiro Costa, Diogo (författare)
- KTH Royal Inst Technol, Stockholm, Sweden.;Westinghouse Elect Sweden AB, Västerås, Sweden.
-
- Naim Katea, Sarmad (författare)
- Uppsala universitet,Oorganisk kemi,Höganäs Sweden AB, Höganäs, Sweden
-
- Jolkkonen, Mikael (författare)
- KTH Royal Inst Technol, Stockholm, Sweden.
-
- Westin, Gunnar, Professor, 1961- (författare)
- Uppsala universitet,Oorganisk kemi
-
- Thuvander, Mattias (författare)
- Chalmers Univ Technol, Gothenburg, Sweden.
-
- Primetzhofer, Daniel (författare)
- Uppsala universitet,Tillämpad kärnfysik,Materialfysik
-
Olsson, Pär (författare)
-
visa färre...
-
KTH Royal Inst Technol, Stockholm, Sweden;KTH Royal Inst Technol, Corresponding author Phys Dept, Nucl Sci & Engn, S-10691 Stockholm, Sweden. KTH Royal Inst Technol, Stockholm, Sweden. (creator_code:org_t)
- Elsevier, 2024
- 2024
- Engelska.
-
Ingår i: Journal of Materiomics. - : Elsevier. - 2352-8478 .- 2352-8486. ; 10:4, s. 906-918
- Relaterad länk:
-
https://doi.org/10.1...
-
visa fler...
-
https://uu.diva-port... (primary) (Raw object)
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Proton irradiation with a primary ion energy of 2 MeV was used to simulate radiation damage in UN and (U,Zr)N fuel pellets. The pellets, nominally at room temperature, were irradiated to peak levels of 0.1, 1, 10 dpa and 100.0 dpa resulting in a peak hydrogen concentration of at most 90 at. %. Microstructure and mechanical properties of the samples were investigated and compared before and after irradiation. The irradiation induced an increase in hardness, whereas a decrease in Young’s modulus was observed for both samples. Microstructural characterization revealed irradiation-induced cracking, initiated in the bulk of the material, where the peak damage was deposited, propagating towards the surface. Additionally, transmission electron microscopy was used to study irradiation defects. Dislocation loops and fringes were identified and observed to increase in density with increasing dose levels. The high density of irradiation defects and hydrogen implanted are proposed as the main cause of swelling and consequent sample cracking, leading simultaneously to increased hardening and a decrease in Young's modulus.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
- NATURVETENSKAP -- Fysik -- Subatomär fysik (hsv//swe)
- NATURAL SCIENCES -- Physical Sciences -- Subatomic Physics (hsv//eng)
Nyckelord
- Proton irradiation
- Uranium nitride
- Spark plasma sintering
- Irradiation induced cracking
- Simulated burn-up structure
- Composite nuclear fuels
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Charatsidou, Eli ...
-
Giamouridou, Mar ...
-
Fazi, Andrea
-
Nagy, Gyula
-
Ribeiro Costa, D ...
-
Naim Katea, Sarm ...
-
visa fler...
-
Jolkkonen, Mikae ...
-
Westin, Gunnar, ...
-
Thuvander, Matti ...
-
Primetzhofer, Da ...
-
Olsson, Pär
-
visa färre...
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Materialteknik
-
och Metallurgi och m ...
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Fysik
-
och Subatomär fysik
- Artiklar i publikationen
-
Journal of Mater ...
- Av lärosätet
-
Uppsala universitet