Microstructural investigation of the initial oxidation of the FeCrAlRE alloy Kanthal AF in dry and wet O2 at 600 and 800°C
-
Canovic, Sead (författare)
-
- Engkvist, Josefin (författare)
- Högskolan Dalarna,Materialvetenskap
-
Liu, Fang (författare)
-
visa fler...
-
Götlind, Helena (författare)
-
Hellström, Kristina (författare)
-
Svensson, Jan-Erik (författare)
-
Johansson, Lars-Gunnar (författare)
-
- Olsson, Mikael (författare)
- Högskolan Dalarna,Materialvetenskap
-
Halvarsson, Mats (författare)
-
visa färre...
-
(creator_code:org_t)
- The electrochemical society, 2010
- 2010
- Engelska.
-
Ingår i: Journal of the Electrochemical Society. - : The electrochemical society. - 0013-4651 .- 1945-7111. ; 157:6, s. C223-C230
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The FeCrAlRE (where RE is reactive element) alloy Kanthal AF was exposed isothermally at 600 and 800°C for 72 h in dry O2 and in O2 with 10 vol % H2O. The mass gains were 3–5 times higher at the higher temperature. The presence of water vapor increased the oxidation rate at 800°C, while no significant effect was observed at 600°C. A thin two-layered oxide formed at 600°C: an outer (Fe,Cr)2O3 corundum-type oxide, containing some Al, and an inner, probably amorphous, Al-rich oxide. At 800°C a two-layered oxide formed in both environments. The inner layer consisted of inward grown a-Al2O3. In dry O2 the originally formed outward grown g-Al2O3 had transformed to a-Al2O3 after 72 h. Water vapor stabilized the outward grown g-Al2O3 and hence no transformation occurred after 72 h in humid environment. RE-rich oxide particles with varying composition (Y, Zr, and Ti) were distributed in the base oxide at both temperatures and in both environments. The RE-rich particles were separated from the alloy substrate by a layer of Al-rich oxide. At 800°C the Y-rich RE particles were surrounded by thick oxide patches in both dry and humid O2.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
Nyckelord
- FeCrAl-legering
- högtemperaturoxidation
- transmissionselektronmikroskopi
- Steel Forming and Surface Engineering
- Stålformning och ytteknik
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas