Importance of Ca(2+) Modifications for Osseointegration of Smooth and Moderately Rough Anodized Titanium Implants - A Removal Torque and Histological Evaluation in Rabbit.
-
- Fröjd, Victoria, 1986 (författare)
- Gothenburg University,Göteborgs universitet,Institutionen för kliniska vetenskaper, Avdelningen för biomaterialvetenskap,Institute of Clinical Sciences, Department of Biomaterials
-
- Wennerberg, Ann, 1955 (författare)
- Malmö högskola,Gothenburg University,Göteborgs universitet,Institutionen för kliniska vetenskaper, Avdelningen för biomaterialvetenskap,Institute of Clinical Sciences, Department of Biomaterials,Odontologiska fakulteten (OD)
-
- Franke Stenport, Victoria, 1970 (författare)
- Gothenburg University,Göteborgs universitet,Institutionen för odontologi,Institute of Odontology
-
(creator_code:org_t)
- 2010-10-26
- 2012
- Engelska.
-
Ingår i: Clinical implant dentistry and related research. - : Wiley. - 1708-8208 .- 1523-0899. ; 14:5, s. 737-745
- Relaterad länk:
-
https://gup.ub.gu.se...
-
visa fler...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- Background: Incorporation of Ca(2+) into the titania of anodized titanium surfaces has been found to enhance osseointegration. It provides a stable surface when the ions are incorporated into the oxide layer during the anodizing process. The Ca(2+) may suggestively be prominent sites for mineral induction, attract proteins, and catalyze intracellular cascades. Purpose: The aim of the present study was to evaluate the osseointegration of smooth (S(a) < 0.5µm) and moderately rough (S(a) 1.0-2.0µm) commercially pure titanium implants, with and without Ca(2+) , in order to reflect on the importance of surface chemistry in relation to topography. Materials and Methods: Anodized implants with (OxCa) or without Ca(2+) (Ox), blasted implants (Bl), and blasted anodized implants, with (BlOxCa) or without Ca(2+) (BlOx), were inserted in rabbit femur and tibia. The implant surfaces were characterized using interferometry, scanning electron microscopy, and X-ray photoelectron spectroscopy prior to implant installation. Removal torque (RTQ) measurements were executed on all implants after a healing period of 12 weeks. The implants were, thereafter, removed en bloc with surrounding tissues and prepared for histological evaluations. Results: RTQ measurements of tibial implants revealed significantly higher values for BlOxCa implants (90.7 ± 23.3 Ncm) compared to OxCa (64.6 ± 18.2 Ncm) and BlOx implants (69.7 ± 17.5 Ncm) (p = 0.029). Ca(2+) modification of smooth implants placed in the femur did not reveal any differences. Conclusion: Ca(2+) modification of smooth implants resulted in similar interfacial shear strength as moderately rough implants and Ca(2+) modification of moderately rough implants demonstrated the significantly strongest interfacial shear strength when placed in rabbit tibia. This possibly demonstrated surface chemistry compensating for lesser roughness.
Ämnesord
- MEDICIN OCH HÄLSOVETENSKAP -- Klinisk medicin -- Odontologi (hsv//swe)
- MEDICAL AND HEALTH SCIENCES -- Clinical Medicine -- Dentistry (hsv//eng)
Nyckelord
- calcium; dental implants; implant surfaces