Direct and reverse mechanical modeling of an alkyd acrylic hybrid system: A morphological study

Colombini, Didier (författare): Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH

Jowkar Deriss, Mehrnoush (författare): Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH

Karlsson, Ola (författare): Lund University,Lunds universitet,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH

Maurer, Frans (författare): Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH

(creator_code:org_t)

2004-03-02
2004
Engelska.
Ingår i: Macromolecules. - : American Chemical Society (ACS). - 0024-9297 .- 1520-5835. ; 37:7, s. 2596-2602

Relaterad länk:: http://dx.doi.org/10...; visa fler...; https://lup.lub.lu.s...; https://doi.org/10.1...; visa färre...

Abstract Ämnesord

Stäng

Mechanical modeling and dynamic mechanical analysis were associated to investigate the viscoelastic properties of an alkyd acrylic hybrid system in connection with its morphology, which was characterized by transmission electron microscopy. Theoretical predictions based on the interlayer model used in direct mode were successfully combined with the experimental viscoelastic data to lead to relevant additional information about the complex particulate morphology of the hybrid system. Thus, using direct mechanical modeling, it was concluded that the experimental response of the alkyd acrylic hybrid system to a sinusoidal mechanical stress corresponds to the mechanical response of a sample whose morphology involves a acrylic-rich interphase between continuous and dispersed alkyd-rich domains. For the very first time, the interlayer model was then used in reverse mode in order to separate the actual viscoelastic properties of such a acrylic-rich interphase from those experimentally obtained for the alkyd acrylic hybrid system. The differences in these extracted viscoelastic properties, when compared to those of the pure latex film, were presented as reflecting the changes in the molecular mobility of the macromolecules resulting from the mutual influence of the phases in the multiphase hybrid material.

Av författaren/redakt...: Colombini, Didie ...; Jowkar Deriss, M ...; Karlsson, Ola; Maurer, Frans

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.