X-ray diffraction reveals the amount of strain and homogeneity of extremely bent single nanowires
-
- Davtyan, Arman (författare)
- University of Siegen
-
- Kriegner, Dominik (författare)
- Dresden University of Technology
-
- Holý, Václav (författare)
- Charles University in Prague
-
visa fler...
-
- AlHassan, Ali (författare)
- University of Siegen
-
- Lewis, Ryan B. (författare)
- McMaster University,Forschungsverbund Berlin e.V. (FVB)
-
- McDermott, Spencer (författare)
- McMaster University
-
- Geelhaar, Lutz (författare)
- Forschungsverbund Berlin e.V. (FVB)
-
- Bahrami, Danial (författare)
- University of Siegen
-
- Anjum, Taseer (författare)
- University of Siegen
-
- Ren, Zhe (författare)
- Lund University,Lunds universitet,Synkrotronljusfysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Synchrotron Radiation Research,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
-
- Richter, Carsten (författare)
- European Synchrotron Radiation Facility
-
- Novikov, Dmitri (författare)
- German Electron Synchrotron (DESY)
-
- Müller, Julian (författare)
- University of Siegen
-
- Butz, Benjamin (författare)
- University of Siegen
-
- Pietsch, Ullrich (författare)
- University of Siegen
-
visa färre...
-
(creator_code:org_t)
- 2020
- 2020
- Engelska 11 s.
-
Ingår i: Journal of Applied Crystallography. - 0021-8898. ; 53, s. 1310-1320
- Relaterad länk:
-
http://dx.doi.org/10... (free)
-
visa fler...
-
https://lup.lub.lu.s...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Core-shell nanowires (NWs) with asymmetric shells allow for strain engineering of NW properties because of the bending resulting from the lattice mismatch between core and shell material. The bending of NWs can be readily observed by electron microscopy. Using X-ray diffraction analysis with a micro- and nano-focused beam, the bending radii found by the microscopic investigations are confirmed and the strain in the NW core is analyzed. For that purpose, a kinematical diffraction theory for highly bent crystals is developed. The homogeneity of the bending and strain is studied along the growth axis of the NWs, and it is found that the lower parts, i.e. close to the substrate/wire interface, are bent less than the parts further up. Extreme bending radii down to ∼3 μm resulting in strain variation of ∼2.5% in the NW core are found.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Nanoteknik -- Nanoteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Nano-technology -- Nano-technology (hsv//eng)
Nyckelord
- Bent crystals
- Nano-focused X-ray beams
- Nanowires
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Davtyan, Arman
-
Kriegner, Domini ...
-
Holý, Václav
-
AlHassan, Ali
-
Lewis, Ryan B.
-
McDermott, Spenc ...
-
visa fler...
-
Geelhaar, Lutz
-
Bahrami, Danial
-
Anjum, Taseer
-
Ren, Zhe
-
Richter, Carsten
-
Novikov, Dmitri
-
Müller, Julian
-
Butz, Benjamin
-
Pietsch, Ullrich
-
visa färre...
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Nanoteknik
-
och Nanoteknik
- Artiklar i publikationen
-
Journal of Appli ...
- Av lärosätet
-
Lunds universitet