Influence of heat pretreatment on ultrafiltration of a solution containing hemicelluloses extracted from wheat bran
-
- Arkell, Anders (författare)
- Lund University,Lunds universitet,Avdelningen för kemiteknik,Institutionen för processteknik och tillämpad biovetenskap,Institutioner vid LTH,Lunds Tekniska Högskola,Division of Chemical Engineering,Department of Process and Life Science Engineering,Departments at LTH,Faculty of Engineering, LTH
-
- Krawczyk, Holger (författare)
- Lund University,Lunds universitet,Avdelningen för kemiteknik,Institutionen för processteknik och tillämpad biovetenskap,Institutioner vid LTH,Lunds Tekniska Högskola,Division of Chemical Engineering,Department of Process and Life Science Engineering,Departments at LTH,Faculty of Engineering, LTH
-
- Jönsson, Ann-Sofi (författare)
- Lund University,Lunds universitet,Avdelningen för kemiteknik,Institutionen för processteknik och tillämpad biovetenskap,Institutioner vid LTH,Lunds Tekniska Högskola,Division of Chemical Engineering,Department of Process and Life Science Engineering,Departments at LTH,Faculty of Engineering, LTH
-
(creator_code:org_t)
- Elsevier BV, 2013
- 2013
- Engelska.
-
Ingår i: Separation and Purification Technology. - : Elsevier BV. - 1873-3794 .- 1383-5866. ; 119, s. 46-50
- Relaterad länk:
-
http://www.sciencedi... (free)
-
visa fler...
-
http://dx.doi.org/10...
-
https://lup.lub.lu.s...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Hemicelluloses extracted from wheat bran can be concentrated and purified by ultrafiltration. However, the viscosity of the process solution is rather high (about 5 mPa s at 80 C and a shear rate of 100 s1), which results in a relatively low flux. The solution was subjected to heat pretreatment in an attempt to decrease the viscosity and increase the flux. Pretreatment of the solution at 80 C for 72 h was found to reduce the viscosity by 25%. The flux during ultrafiltration with a 10 kDa ceramic membrane increased from 48 l/m2 h, for the untreated solution, to 62 l/m2 h. The increase in flux was lower than expected, and this was attributed to the formation of a fouling layer of acid-insoluble compounds on the membrane. Both hemicelluloses and lignin were partly degraded. The retention of lignin was reduced from about 30% to 18%, whereas the retention of hemicelluloses was above 95%, and was not affected by heat pretreatment. The decrease in lignin retention after heat pretreatment results in improved separation of hemicelluloses and lignin, facilitating the purification of hemicelluloses.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering (hsv//eng)
Nyckelord
- Ultrafiltration
- Ceramic membrane
- Hemicelluloses
- Wheat bran
- Heat pretreatment