Fracture characteristics of acetylated young Scots pine
-
- Forsman, Karin (författare)
- Lund University,Lunds universitet,Byggnadsmekanik,Institutionen för byggvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Structural Mechanics,Department of Construction Sciences,Departments at LTH,Faculty of Engineering, LTH
-
- Serrano, Erik (författare)
- Lund University,Lunds universitet,Byggnadsmekanik,Institutionen för byggvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Structural Mechanics,Department of Construction Sciences,Departments at LTH,Faculty of Engineering, LTH
-
- Danielsson, Henrik (författare)
- Lund University,Lunds universitet,Byggnadsmekanik,Institutionen för byggvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Structural Mechanics,Department of Construction Sciences,Departments at LTH,Faculty of Engineering, LTH
-
visa fler...
-
- Engqvist, Jonas (författare)
- Lund University,Lunds universitet,Hållfasthetslära,Institutionen för byggvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Solid Mechanics,Department of Construction Sciences,Departments at LTH,Faculty of Engineering, LTH
-
visa färre...
-
(creator_code:org_t)
- 2020-06-19
- 2020
- Engelska 11 s.
-
Ingår i: European Journal of Wood and Wood Products. - : Springer Science and Business Media LLC. - 0018-3768 .- 1436-736X. ; 78:4, s. 693-703
- Relaterad länk:
-
http://dx.doi.org/10... (free)
-
visa fler...
-
https://link.springe...
-
https://lup.lub.lu.s...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- A study on the fracture characteristics of unmodified and chemically modified Scots pine (Pinus sylvestris) is presented. The investigated material consisted of small-dimension sawn timber originating from young logs (thinnings), aged 30–40 years. The modified samples were acetylated with acetic anhydride in an industrial scale process without the use of any catalyst, reaching an acetyl content of approximately 20%. Clear wood specimens, consisting of either heartwood or sapwood, were extracted and conditioned to equilibrium at a relative humidity of 60% and a temperature of 20 °C. The fracture energy for mode I loading in tension perpendicular to the grain was determined using single edge notched beam (SENB) specimens, subjected to three-point bending. Additionally, the modulus of elasticity along the grain and the tensile strength perpendicular to the grain were determined for sapwood specimens. The findings demonstrated a significant decrease (between 36 and 50%) in the fracture energy for the acetylated specimens, compared to the unmodified specimens. No significant effect of the acetylation process on the modulus of elasticity, nor on the tensile strength could be concluded. This study indicates that the acetylation process used results in an increased brittleness for Scots pine. Further studies are needed to analyse why the fracture energy is impaired, and to examine whether and how current timber engineering design provisions can or should be revised to account for the increased brittleness of acetylated Scots pine.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Maskinteknik -- Teknisk mekanik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Mechanical Engineering -- Applied Mechanics (hsv//eng)
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas